Abstract:β‐Si3N4 ceramics with an additive oxide system of 1 wt% MgO and 3 wt% Re2O3 (Re = Gd, La, Y and Yb) were fabricated by liquid phase sintering at 1950°C under nitrogen pressure of 748 kPa. Starting α‐Si3N4 powder with 10 vol% rod‐like β‐Si3N4 seed crystallites and an extended sintering time from 5 to 40 h resulted in the formation of bimodal microstructure composed of fine matrix grains and large grains. The 40 h‐sintered specimens of pseudo ternary β‐Si3N4‐MgO‐Gd2O3 system exhibited enhanced thermal conductivity of 127.2 ± 2.5 W m−1 K−1 associated with a degradation of the fracture strength from 1008.0 ± 38.0 to 491.7 ± 32.0 MPa, which was due to the formation of coarse‐grained aggregates that acted as both fracture origin as well as a thermal conductive pathway. The theoretical thermal conductivity was predicted for the sintered specimens by using equations based on a mean‐field micromechanics model to estimate the effective thermal conductivity of each component of binary composites. The calculation results suggested that the thermal conductivity of the large β‐Si3N4 grains (≥ 2 μm in diameter) was relatively high and estimated to be in the range of 175 to 191 Wm−1 K−1.The improved thermal conductivity of the 40 h‐sintered specimens was further discussed for the series of β‐Si3N4‐MgO‐Re2O3 systems based on the nanostructure characterization results obtained by the high‐resolution transmission electron microscopy and scanning transmission electron microscopy‐energy dispersive X‐ray spectrometry analyses. This article is protected by copyright. All rights reserved

Effects of seeds on the thermal conductivity of self-toughened Si3N4 ceramics

Effect of the Residual Phases in Β-Si3n4 Seed on the Mechanical Properties of Self-Reinforced Si3N4 Ceramics

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Effects of β-Si3N4 seeds addition on microstructure and mechanical properties of porous Si3N4 ceramics

Effects of α-Si3N4 seeds and sintering additives on properties of porous silicon nitride ceramics fabricated by carbothermal reduction

Preparation of β-Si3N4 Seeds and Self-reinforced Si3N4 Ceramics

Effect of β-Si<sub>3</sub>N<sub>4</sub> Powder on Thermal Conductivity of Silicon Nitride Ceramics

Thermal conductivity improvement in Si3N4 ceramics via grain purification

Effects of MgSiN2 Addition and Post-Annealing on Mechanical and Thermal Properties of Si3N4 Ceramics

Effect of Seed Crystal Properties on the Microstructure of Si<sub>3</sub>N<sub>4</sub> Ceramics

Mechanical Property and Oxidation Behavior of Self-Reinforced Si3N4 Doped with Re2O3 (Re=Yb, Lu)

Preparation of the rod-like {beta}-Si{sub 3}N{sub 4} particles favoring the self-reinforcing Si{sub 3}N{sub 4} ceramics

Effect of Post-Sintering Heat-Treatment on Thermal Conductivity of Si3N4 Ceramics Containing Different Additives

Study on microstructure and mechanical properties of porous Si3N4 ceramics

Effect of CeO2, Dy2O3, Yb 2O3 and y2O3 additives on thermal conductivity of silicon nitride ceramics

Fabrication and Characterization of β-Si3N4 Seeds with Additive of Lu2O3

Effects of Sintering Additive and Β-Si3n4 Phase Contents on the Properties of Porous Si3N4 Ceramics

Influence of Stabilizing Ions and Sintering Process on the Thermal Conductivity of Α‐sialon Ceramics

Sintering behavior and properties of Si 3N 4 ceramics with yttrium chloride additive

Effect Of Microstructural Modification On Thermal Conductivity And Strength Of Silicon Nitride