Abstract:This paper introduces an approach to preparing high‐strength Si3N4 ceramics using vat photopolymerization with a bi‐phase particle size gradation strategy. The influence of different ratios of coarse β‐Si3N4 powders (Cβ) and fine α‐Si3N4 powders (Fα) on the slurry performance, microstructure evolution, and final ceramic strength was systematically studied. It was found that an appropriate particle size gradation can significantly reduce the viscosity of the slurry. The curing depth of Si3N4 slurries decreases with increasing Fα content, while the stability increases. During sintering, dissolved Fα‐Si3N4 not only directly precipitates into small elongated β‐Si3N4 grains but also onto the neighboring Cβ‐Si3N4, promoting the development of large elongated β‐Si3N4 grains and resulting in a bimodal microstructure distribution. The highest strength of Si3N4 ceramics was achieved with a ratio of 6:4 Cβ to Fα Si3N4 powders. Under these conditions, the Si3N4 ceramics exhibited a flexural strength of 472 MPa, significantly higher than that of Si3N4 ceramics prepared using pure Cβ/Fα powders. The strength improvement is primarily due to the well‐designed bi‐phase particle size gradation strategy, which optimizes slurry performance, minimizes defects that may be introduced during the green part printing process while controlling the microstructure evolution during sintering, achieves the ideal bimodal microstructure distribution. The outcomes of this research demonstrate the feasibility of using vat photopolymerization with bi‐phase particle size gradation for the preparation of high‐strength Si3N4 ceramics, which has great potential for application in the manufacturing of various ceramic products.

Preparation of graded silicon nitride ceramics with high mechanical performance using β-Si 3 N 4 seeds

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

New Route to Improve the Fracture Toughness and Flexural Strength of Si3N4 Ceramics by Adding FeSi2

Effects of α-Si3N4 seeds on properties of porous laminated silicon nitride ceramics

Fabrication of High-Porosity Silicon Nitride Ceramics with Excellent Mechanical Properties

Preparation of β-Si3N4 Seeds and Self-reinforced Si3N4 Ceramics

Investigation of the physical and mechanical properties of hot-pressed machinable Si3N4/h-BN composites and FGM

Advanced Fabrication Method and Mechanical Properties of Silicon Nitride/Boron Nitride Fibrous Monolithic Ceramics

New Progress in the Preparation and Application of High Performance Silicon Nitride Ceramics

Fabrication and characterization of machinable Si3N4/h-BN functionally graded materials

Influence of α-Si3N4 coarse powder on densification, microstructure, mechanical properties, and thermal behavior of silicon nitride ceramics

Microstructure characterization of hot-pressed β-silicon nitride containing β-Si3N4 seeds

Preparation and Characterization of Rod-Like Β-Si<sub>3</sub>n<sub>4</sub> Seeds

Preparation of high‐strength Si3N4 ceramics via vat photopolymerization: A bi‐phase particle size gradation strategy

Simultaneous improvement in porosity and strength of porous β-Si3N4 ceramics by formation of ultrafine fibrous grains

Preparation, Properties and Growth Mechanism of Low-Cost Porous Si3N4 Ceramics with High Levels of β-Si3N4 Powders

Progress in Research and Application of Gas-Pressure-Sintered Silicon Nitride Ceramics

Fabrication of Porous Silicon Nitride Ceramics with Gradient Microstructure

Synthesis and Mechanical Properties of Highly Porous Ultrafine-Grain Si3N4 Ceramics Via Carbothermal Reduction-Nitridation Combined with Liquid Phase Sintering

Digital Light Processing of High-Strength Si3N4 Ceramics: Role of Particle Grading on Slurries Curing and Mechanical Properties

Microstructure and Properties of Si3N4 Ceramics Obtained from Addition of Β-Phase Seeds and Celsian