Abstract:We report here a detailed characterization of the surface chemical states and morphology of polyimide (PI) films following modifications by plasma treatment and electroless copper deposition. NH3 and Ar plasma treatments have been successfully used to achieve morphological and chemical modification of the PI surface so that electroless copper plating can occur. The adhesion strength of the electroless copper to the PI surface was measured and correlated with the plasma-induced chemical and physical modifications of the PI surface. The NH3 plasma causes primarily chemical changes to the PI surface through creation of nitrogen moieties (i.e., –N =C< ) on the surface. The Ar plasma treatment brings about mainly physical changes to the surface (i.e., surface roughening). The combined-plasma treatment (Ar plasma followed by NH3 plasma) combines the desirable chemical and physical effects of each treatment, yielding a PI surface with higher roughness for physical anchoring of the copper and surface bonding sites (nitrogen and oxygen sites). During the electroless copper surface activation step with tin chloride and palladium chloride, tin bonds mainly with the oxygen on the surface, whereas palladium reacts with tin chloride as well as with the surface nitrogen. A direct relationship has been observed between surface palladium concentration and the abundance of the –N =C< sites on the surface. This suggests that the nitrogen radicals created during the NH3 plasma are incorporated into the surface and serve as bonding sites for the palladium. In the subsequent electroless Cu deposition, there was a direct correlation between the palladium surface concentration and Cu coverage. The adhesion strength of the electroless copper to the PI correlated well to the surface modifications and plasma treatment conditions. For the first time, a specific bonding configuration on the PI surface is shown to promote adsorption of palladium, which in turn promotes covalent bonding with Cu. The relative importance of surface roughness and chemical bonding on the adhesion strength is discussed.

Diffusion and Adhesion Properties of Cu Films on Polyimide Substrates

Effect of heat treatment on the peel strength of two kinds of Cu film

Effect of heat treatment on TiN diffusion barriers in copper thin film metallization on PI substrates

Study on interface behavior of Be/CuCrZr alloy by diffusion bonding

Nucleation and growth of low resistivity copper thin films on polyimide substrates by low-temperature atomic layer deposition

Adhesive properties of deposited Cu films on colorless polyimide using high power impulse magnetron sputtering system

Irradiation Behaviors of TiN Diffusion Barriers in Cu/PI Substrates

Properties of Cu Film and Ti/Cu Film on Polyimide Prepared by Ion Beam Techniques

Sputtered Ru–Ti, Ru–N and Ru–Ti–N Films As Cu Diffusion Barrier

A New Method to Obtain Cu Films with Lower Resistivity and Higher Interface Adhesion on Different Substrates

Internal Stress and Adhesion of Cu Film/Si Prepared by Both Mevva and Ibad

Studies of Polyimide/copper Interface and Its Improvement by a Two‐component Primer

Plasma Treatment and Surface Analysis of Polyimide Films for Electroless Copper Buildup Process

Ti–Cu Coatings Deposited by a Combination of HiPIMS and DC Magnetron Sputtering: The Role of Vacuum Annealing on Cu Diffusion, Microstructure, and Corrosion Resistance

Effect of surface roughness on the adhesion properties of Cu/Cr films on polyimide substrate treated by inductively coupled oxygen plasma

Plasma surface pretreatment to improve interfacial adhesion strengths of sputtered Cu on polyimide film

Modification of Cu Nanoparticles with A Disulfide for Polyimide Metallization

Adhesion and Transparency Enhancement between Flexible Polyimide-PDMS Copolymerized Film and Copper Foil for LED Transparent Screen

Effect of High-Frequency and High-Density Current on Adhesive Strength of Copper Thin Film

Surface Modification of Copper for Adhesion Promotion by Polybenzimidazole

Grafting Amino Groups onto Polyimide Films in Flexible Copper-Clad Laminates Using Helicon Plasma