Abstract:We report here a detailed characterization of the surface chemical states and morphology of polyimide (PI) films following modifications by plasma treatment and electroless copper deposition. NH3 and Ar plasma treatments have been successfully used to achieve morphological and chemical modification of the PI surface so that electroless copper plating can occur. The adhesion strength of the electroless copper to the PI surface was measured and correlated with the plasma-induced chemical and physical modifications of the PI surface. The NH3 plasma causes primarily chemical changes to the PI surface through creation of nitrogen moieties (i.e., –N =C< ) on the surface. The Ar plasma treatment brings about mainly physical changes to the surface (i.e., surface roughening). The combined-plasma treatment (Ar plasma followed by NH3 plasma) combines the desirable chemical and physical effects of each treatment, yielding a PI surface with higher roughness for physical anchoring of the copper and surface bonding sites (nitrogen and oxygen sites). During the electroless copper surface activation step with tin chloride and palladium chloride, tin bonds mainly with the oxygen on the surface, whereas palladium reacts with tin chloride as well as with the surface nitrogen. A direct relationship has been observed between surface palladium concentration and the abundance of the –N =C< sites on the surface. This suggests that the nitrogen radicals created during the NH3 plasma are incorporated into the surface and serve as bonding sites for the palladium. In the subsequent electroless Cu deposition, there was a direct correlation between the palladium surface concentration and Cu coverage. The adhesion strength of the electroless copper to the PI correlated well to the surface modifications and plasma treatment conditions. For the first time, a specific bonding configuration on the PI surface is shown to promote adsorption of palladium, which in turn promotes covalent bonding with Cu. The relative importance of surface roughness and chemical bonding on the adhesion strength is discussed.

Nucleation and growth of low resistivity copper thin films on polyimide substrates by low-temperature atomic layer deposition

Improved Electrical Resistivity of Atomic-Layer-Deposited Copper Thin Films on Polyimide Substrates by an In Situ ZnO Interlayer

Low-Temperature Atomic Layer Deposition of High Purity, Smooth, Low Resistivity Copper Films by Using Amidinate Precursor and Hydrogen Plasma

Electroless Plating of Copper via a Sn-Free Process on Dielectric SiLK Surface Modified by UV-Induced Graft Copolymerization with 4-Vinylpyridine and 1-Vinylimidazole

Diffusion and Adhesion Properties of Cu Films on Polyimide Substrates

Modification of Cu Nanoparticles with A Disulfide for Polyimide Metallization

Grafting Amino Groups onto Polyimide Films in Flexible Copper-Clad Laminates Using Helicon Plasma

Adhesion property between low-thermal- expansion poly (benzoxazole-imide) film and ion-implanted copper

On the Mechanism of the Atomic Layer Deposition of Cu Films on Silicon Oxide Surfaces: Activation Using Atomic Hydrogen and Three-Dimensional Growth

Direct additive copper plating on polyimide surface with silver ammonia via plasma modification

Plasma Treatment and Surface Analysis of Polyimide Films for Electroless Copper Buildup Process

A New Method to Obtain Cu Films with Lower Resistivity and Higher Interface Adhesion on Different Substrates

Emerging Non-Noble-Metal Atomic Layer Deposited Copper as Seeds for Electroless Copper Deposition

In-situ spectroscopic ellipsometry study of copper selective-area atomic layer deposition on palladium

Interlayer Design for Strong Adhesion in the Double-Layer Flexible Copper Clad Laminate Via Hipims Deposition

Copper Metallization on the Surface-Modified Polyimide Films by Electroless Plating Method

Effects of amino-terminated self-assembled monolayers on nucleation and growth of chemical vapor-deposited copper films

Plasma surface pretreatment to improve interfacial adhesion strengths of sputtered Cu on polyimide film

Studies of Polyimide/copper Interface and Its Improvement by a Two‐component Primer

Impact of Surface Hydroxyl Groups on CuO Film Growth by Atomic Layer Deposition

Selective atomic layer deposition on flexible polymeric substrates employing a polyimide adhesive as a physical mask