Abstract:The pressureless-sintering behavior of AIN-SiC ceramics with 2mass% Y2O3 as a sintering aid was investigated. The AIN-SiC composites containing up to 30vol% SiC (two kinds of SiC sources: equiaxed α-SiC and rod-shaped β-SiC particles) were sintered to about 97% of the theoretical density at 2073K in Ar atmosphere of 0.1MPa, and fully densified further by cladless post-HIP-sintering. The mechanical properties including Young's modulus, bending strength and fracture toughness were evaluated for the densely HIPed materials. The Young's modulus was measured from room temperature to 1723K, and the AIN and AIN-SiC composites showed no decrease in Young's modulus at temperatures up to 1473K. The AIN-SiC composites showed increasing bending strength with increasing SiC content, and the highest bending strength was obtained in the AIN-30%SiC composite with rod-shaped β-SiC particles. The fracture toughness of the AIN increased about 60% after the post-HIP treatment due to the toughening effect of elongated grains which was found to be preferably formed in the AIN and AIN-rich composites. The AIN-SiC composites showed no remarkable increase in the fracture toughness with increasing SiC additions, as a result of the decrease in the amount of the elongated grains.

Fabrication of AlN-SiC-TiB2 Ceramics by Self-Propagating High Temperature Synthesis and Hot Isostatic Pressing

Synthesis and Properties of AlN-SiC-TiB2 Ceramics by SHS-HIP

Synthesis and properties of AIN-SiC-TiB2 ceramics by SHS-HIP

Fabrication of BN-AlN-TiB2 Compound Conductive Ceramics by Self-Propagating High Temperature Synthesis and Hot Isostatic Pressing

Microstructure and Mechanical Properties of AlN-TiN-TiB2 Composite Conductive Ceramics

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

Oxidation behavior of AlN–SiC–TiB2 ceramics synthesized by SHS–HIP

Fabrication and properties of Ti3AlC2-based ceramics by two-step method

Dense TiC-Al2O3 composites fabricated by SHS

Fabrication of highly dense Ti3SiC2 ceramics by pressureless sintering of mechanically alloyed elemental powders

Enhanced Mechanical/electrical Properties of in Situ Synthesized SiC-TiB2 Ceramic Composites by Reactive Hot-Pressing Sintering

Synthesis and Mechanical Properties of TiB2/Ti2AlN Composites Fabricated by Hot Pressing Sintering

Mechanical Properties of AlN-SiC Ceramic Composites Synthesized by Pressureless Sintering and Post-HIP Treatment.

Research on TiC-Ni cermets by SHS and pseudo heat isostatic pressing

Synthesis of SiC-AlN Powder and Characterization of Its HIP-Sintered Compacts.

Study on sintering of SHSTi3AlC2 powders by hot pressing

Fabrication and Properties of Ti<sub>3</sub>AlC<sub>2</sub>-Based Ceramics by Two-Step Method

DENSE TiC-Al2O3-Fe CERMET FABRICATED BY SHS

Fabrication and Mechanical Properties of High-Pure Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials Directly by Hot-Pressing its Powder

Fabrication and mechanical properties of high-pure Ti3SiC 2 bulk materials directly by hot-pressing its powder

Fabrication of Si 3 N 4 ceramics with high thermal conductivity and flexural strength via novel two-step gas-pressure sintering