Abstract:Dense polycrystalline Ti3SiC2 samples were fabricated by reactively hot-isostatic pressing (HIPing) a mixture of elemental Ti, Si and C powders. The mechanical properties, including load–strain response, bending strength, fracture toughness and crack propagation, were investigated from ambient temperature to 1573 K. Non-linear stress–strain responses were observed in the polycrystalline Ti3SiC2 materials at ambient temperature. It is conceivable that the inelastic deformation is attributable to micro-deformations that consist of slip between micro-lamellae within individual grains and the formation of microcracks between grains. The polycrystalline Ti3SiC2 exhibited a brittle-to-ductile transition at about 1473 K; above this the Ti3SiC2 samples deformed plastically and exhibited high strains (>1.5%), whereas below 1373 K only limited inelastic deformation was observed prior to fracture. The mode I fracture toughness, KIC, was measured by the single-edge notched beam (SENB) method to be 4.52 MPa m1/2 at ambient temperature. Both fracture strength and fracture toughness decrease only slightly with increasing temperature up to 1273 K, above which they decrease more rapidly and reach half of their room-temperature values by 1473 K.

Fabrication and mechanical properties of high-pure Ti3SiC 2 bulk materials directly by hot-pressing its powder

Fabrication and Mechanical Properties of High-Pure Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials Directly by Hot-Pressing its Powder

Fabrication of highly dense Ti3SiC2 ceramics by pressureless sintering of mechanically alloyed elemental powders

Synthesis of High-Purity Ti3SiC2 Polycrystals by Hot-Pressing of the Elemental Powders

Fabrication of high purity Ti3SiC2 from Ti/Si/C with the aids of Al by spark plasma sintering

Synthesis of High Purity Ti3AlC2 Bulk Material by Hot-Pressing

Fabrication of Ti<sub>3</sub>AlC<sub>2</sub> Powder with High-Purity by Pressureless Sintering

Fabrication of Ti3AlC2 Powder with High-Purity by Pressureless Sintering

Synthesis and Mechanical Properties of In-Situ Hot-Pressed Ti3SiC2 Polycrystals

Fabrication of Ti<sub>3</sub>AlC<sub>2</sub> Powder with High-Purity by Pressureless Sintering

Freeform Fabrication of Ti3SiC2 Structures

Synthesis Of High-Purity Powder Ti3alc2 Materials By Pressureless Sintering

Mechanical properties of short carbon fiber-reinforced TiC composites produced by hot pressing

Preparation of High‐Strength Ti3AlC2 by Spark Plasma Sintering

Study on sintering of SHSTi3AlC2 powders by hot pressing

Preparation and characterization of Ti3SiC2 powder

Freeform Fabrication of Ti3SiC2 Powder-Based Structures

Synthesis of Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials with B<sub>2</sub>O<sub>3</sub> Additive

Mechanical properties of polycrystalline Ti3SiC2 at ambient and elevated temperatures

Fabrication and properties of Ti3AlC2-based ceramics by two-step method

Synthesis of Ti3SiC2 Bulk Materials with B2O3 Additive

Fabrication and mechanical properties of high-pure Ti3SiC 2 bulk materials directly by hot-pressing its powder

Fabrication and Mechanical Properties of High-Pure Ti&lt;sub&gt;3&lt;/sub&gt;SiC&lt;sub&gt;2&lt;/sub&gt; Bulk Materials Directly by Hot-Pressing its Powder

Fabrication of highly dense Ti3SiC2 ceramics by pressureless sintering of mechanically alloyed elemental powders

Synthesis of High-Purity Ti3SiC2 Polycrystals by Hot-Pressing of the Elemental Powders

Fabrication of high purity Ti3SiC2 from Ti/Si/C with the aids of Al by spark plasma sintering

Synthesis of High Purity Ti3AlC2 Bulk Material by Hot-Pressing

Fabrication of Ti&lt;sub&gt;3&lt;/sub&gt;AlC&lt;sub&gt;2&lt;/sub&gt; Powder with High-Purity by Pressureless Sintering

Fabrication of Ti3AlC2 Powder with High-Purity by Pressureless Sintering

Synthesis and Mechanical Properties of In-Situ Hot-Pressed Ti3SiC2 Polycrystals

Fabrication of Ti<sub>3</sub>AlC<sub>2</sub> Powder with High-Purity by Pressureless Sintering

Freeform Fabrication of Ti3SiC2 Structures

Synthesis Of High-Purity Powder Ti3alc2 Materials By Pressureless Sintering

Mechanical properties of short carbon fiber-reinforced TiC composites produced by hot pressing

Preparation of High‐Strength Ti3AlC2 by Spark Plasma Sintering

Study on sintering of SHSTi3AlC2 powders by hot pressing

Preparation and characterization of Ti3SiC2 powder

Freeform Fabrication of Ti3SiC2 Powder-Based Structures

Synthesis of Ti&lt;sub&gt;3&lt;/sub&gt;SiC&lt;sub&gt;2&lt;/sub&gt; Bulk Materials with B&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;3&lt;/sub&gt; Additive

Mechanical properties of polycrystalline Ti3SiC2 at ambient and elevated temperatures

Fabrication and properties of Ti3AlC2-based ceramics by two-step method

Synthesis of Ti3SiC2 Bulk Materials with B2O3 Additive

Fabrication and Mechanical Properties of High-Pure Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials Directly by Hot-Pressing its Powder

Fabrication of Ti<sub>3</sub>AlC<sub>2</sub> Powder with High-Purity by Pressureless Sintering

Synthesis of Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials with B<sub>2</sub>O<sub>3</sub> Additive