Abstract:Titanium metal matrix composite microlattices are fabricated using 3D ink extrusion printing and sintering. The inks consist of TiH2+TiB2 or TiH2+TiC powder blends to form (i) Ti-TiB composites by dehydrogenation and in situ reaction of Ti + TiB2 to form Ti + TiB and (ii) Ti-TiC composites, where TiC remains stable during the sintering process. Rapid densification of the printed powder blend is achieved during pressureless sintering in vacuum at 1200 °C between 1 and 4 h, due to the small Ti particle size available from dehydrogenation of micron-sized TiH2. Near-full density Ti-TiB and Ti-TiC is achieved within individual lattice struts, despite high TiB and TiC volume fractions up to 25 vol.%. The added TiB2 particles are fully dissolved and re-precipitated to TiB whiskers and whisker clusters in <0.5 h. The compressive properties of sintered cross-ply microlattices are measured for the three types of composites (Ti-TiB, Ti-TiC and Ti-TiC(W), with W originating from powder contamination) and pure Ti controls as a function of lattice orientation with respect to load. The compressive strength of the Ti-TiB/TiC composites increases from 55 to 1019 MPa as the designed lattice macroporosity is reduced from 71 to 24 %, and scales with the third power of relative density, indicating a high sensitivity of strength with relative density.

Freeform Fabrication of Ti3SiC2 Powder-Based Structures

Freeform Fabrication of Ti3SiC2 Structures

Fabrication of Fully Dense Tial-Based Composite Sheets with A Novel Microlaminated Microstructure

Fabrication of highly dense Ti3SiC2 ceramics by pressureless sintering of mechanically alloyed elemental powders

Fabrication and Mechanical Properties of High-Pure Ti<sub>3</sub>SiC<sub>2</sub> Bulk Materials Directly by Hot-Pressing its Powder

Fabrication and mechanical properties of high-pure Ti3SiC 2 bulk materials directly by hot-pressing its powder

Fabrication and Properties of TiC/Ti<sub>3</sub>SiC<sub>2</sub> Composites and FGMs

Fabrication and characterization of carbon fiber reinforced SiC ceramic matrix composites based on 3D printing technology

Fabrication and properties of TiC/Ti3SiC2 composites and FGMs

POLYMER-DERIVED SIC CERAMIC WITH TRIPLY PERIOD MINIMAL SURFACE STRUCTURE FABRICATION THROUGH DIGITAL LIGHT PROCESSING

Fabrication and properties of Ti3AlC2-based ceramics by two-step method

The Preparation of TiC/TiN Composites by Selective Laser Melting

Fabrication and Properties of Ti<sub>3</sub>AlC<sub>2</sub>-Based Ceramics by Two-Step Method

Preparation and properties of Ti3SiC2 preform reinforced SiC ceramic matrix composites

Fabrication and properties of TiC-high manganese steel cermet processed by 3D gel printing

Geometrically Complex Silicon Carbide Structures Fabricated by Robocasting

3D ink-extrusion printing and sintering of Ti, Ti-TiB and Ti-TiC microlattices

Stereolithography-based additive manufacturing of lightweight and high-strength Cf/SiC ceramics

Complex SiC-based structures with high specific strength fabricated by vat photopolymerization and one-step pyrolysis

High-strength and low-silicon SiC ceramics prepared by extrusion molding 3D printing

Efficient fabrication and properties of 2D Cf/(Ti0.2Zr0.2Hf0.2Nb0.2Ta0.2)C-SiC high-entropy ceramic matrix composites via slurry infiltration lamination combined with precursor infiltration and pyrolysis