Phase Formation, Microstructure and Mechanical Properties of TaB2-SiC Composites Synthesized by Reaction Hot Pressing: Effects of SiC Contents and Oxygen Impurity
Yonghui Yu,Jie Wei,Xianghui Yan,Yuhong Chen,Biao Zhang,Yujin Wang,Feng Ye,Limeng Liu
DOI: https://doi.org/10.1016/j.matchemphys.2024.129949
IF: 4.778
2024-01-01
Materials Chemistry and Physics
Abstract:TaB2-SiC composites with 0-20 wt% SiC contents were prepared by reaction hot pressing using Ta, B and SiC powders as starting materials. Densification, constituent phases, microstructure and mechanical properties, namely Vickers hardness, fracture toughness and flexure strength, were evaluated by means of inspection of sintering shrinkage, density measurement, XRD, SEM, TEM, HRTEM, EDS, SAED, indentation and three-point bending tests. Phase formation, including dominant (TaB2, SiC) and minor (TaC, glassy SiO2) phases, was checked by thermodynamic assessment relevant with Ta2O5 and B2O3 impurities introduced into the reaction system by the starting powders. The results showed that mixtures of Ta, B and SiC powders would initiate self-propagating combustion synthesis (SPCS) at about 900 degrees C; a transient hold at 800 degrees C for 1 h could suppress this reaction. Volatilization of B2O3 impurity in association with local high temperature due to SPCS helped reduce the TaC and glassy SiO2 minor phase formation. TaB2-SiC composites could reach 99 % relative densities with 3 wt% SiC addition and above. Compositions with <7.5 wt% SiC additions showed uniform dispersion of SiC particles at multi-TaB2 grain junctions while compositions with higher SiC content revealed SiC segregation. Bending strength of 503 MPa and fracture toughness of 6.69 MPa & sdot;m(1/2) could be reached with 7.5-20 wt% SiC addition.