Abstract:Ti3SiC2 compound can enhance the oxidation resistance of C/C composites as a modifying material, thanks for its superior high-temperature stability, indicating significant potential for applications. In this work, titanium powder and liquid polycarbosilane (LPCS) were served as starting materials for producing Ti3SiC2 ceramics with four different phase contents by polymer derived ceramics (PDC) method at temperatures of 1200, 1300, 1400, and 1500 degrees C, respectively. Effects of sintering temperature on the phase compositions and morphology of the ceramics were studied. Additionally, the impact of varying Ti3SiC2 phase contents on oxidation resistance and thermal shock resistance were also explored. The results showed that layered Ti3SiC2 formed at Ti : Si molar ratio of 3 : 1.5 when sintered at 1300, 1400, and 1500 degrees C, respectively. After sintered at 1400 degrees C, the mass fraction of Ti3SiC2 in the ceramic product reached 92.10% with the bending strength of 172.68 MPa. When subjected to a static air environment of 1300 degrees C for 7 h, the oxidation weight of the ceramics obtained progressively reduction with the increase of Ti3SiC2 phase content. During the oxidation process, a protective film primarily consisted of TiO2 was formed on the surface, which effectively slowed down the oxygen diffusion into the interior. Air thermal shock tests at 1300 degrees C and flexural strength assessments demonstrated that the residual strength of all materials decreased with the increase of thermal shock times. Nevertheless, the thermal shock resistance and residual strength of the samples were enhanced with the increase of Ti3SiC2 phase content. After 30 times thermal shock, the sample with the mass fraction of Ti3SiC2 phase of 92.10% experienced 30.66% weight loss and retained residual strength of 120.18 MPa, primarily due to the layered structure of Ti3SiC2 which is significantly extends the crack propagation path and its superior oxidation resistance.

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

Preparation of titanium carbide powders by sol–gel and microwave carbothermal reduction methods at low temperature

Preparation of Titanium Carbide by Carburisation of Titanium Dioxide

Investigation of TiC formation during ball-milling of elemental titanium and carbon

Preparation of Titanium Carbonitride Powder by Carbothermal Reduction Method

Preparation of Nano-TiC Powders by In-situ Carbothermal Method in Vacuum

Preparation and Thermal Stability of Ti3SiC2 Ceramics by Polymer Derived Ceramics Method

Effect of Powder Synthesis Processing on Microstructure and Mechanical Properties of TiB2-TiC Composite Ceramics

Synthesis and Characterization of TiC Nanopowders Via Sol-Gel and Subsequent Carbothermal Reduction Process

Effects of sintering temperature and Si content on the purity of Ti3SiC2 synthesized from Ti/Si/TiC powders

Facile Synthesis of Ti3SiC2 Powder by High Energy Ball-Milling and Vacuum Pressureless Heat-Treating Process from Ti–TiC–SiC–Al Powder Mixtures

Synthesis and Sintering of Tungsten and Titanium Carbide: A Parametric Study

Synthesis of TiC Powder by Carbothermal Reduction and Phase Evolution

Preparation and Properties of Solidified TiC-TiB2 with Hypoeutectic, Eutectic and Hypereutectic Microstructures

Reactive Synthesis of Polycrystalline Ti3AlC2 and Its Sintering Behavior

Progress in Preparation and Application of Ultrafine TiC Powder

Preparations of Titanium Nitride, Titanium Carbonitride and Titanium Carbide Via a Two-Step Carbothermic Reduction Method

Studies on the carbothermal preparation of titanium carbonitride powders in the open system

Preparation and characterization of Ti3SiC2 powder

Research on Synthesis of TiC by Taking Phenol-formaldehyde Resins As Carbon Resource

Microstructure, Mechanical Property and Thermal Conductivity of Porous TiCO Ceramic Fabricated by In Situ Carbothermal Reduction of Phenolic Resin and Titania