Abstract:The use of metal-coated ceramic powders not only effectively enhances the wettability of the metal–ceramic interface but also promotes a more uniform microstructure in Ti(C,N)-based cermets, which is advantageous for improving their mechanical properties. In this study, ultrafine Co- and Ni-coated (Ti,W,Mo,Ta)(C,N) powders were synthesized via the spray-drying-in-situ carbothermal reduction method. Subsequently, Ti(C,N)-based cermets were effectively fabricated using the as-prepared ultrafine Co- and Ni-coated (Ti,W,Mo,Ta)(C,N) powders. The impact of reaction temperature, heating rate, and isothermal time on the phase and microstructure of prepared powders was analyzed using X-ray diffraction (XRD), scanning electron microscopy (SEM), and transmission electron microscopy (TEM). Additionally, the microstructure of the as-sintered cermets was experimentally investigated. The findings reveal that the complete reduction of Co and Ni metal salts, pre-coated on the surface of (Ti,W,Mo,Ta)(C,N) particles, can be achieved through rapid heating (10 °C/min) in a specific temperature range (600–1000 °C) with an isothermal time of 3 h at a lower reduction temperature (1000 °C). The synthesized powders have only two phases: the (Ti,W,Mo,Ta)(C,N) phase and Co/Ni phase, and no other heterogeneous phases were observed with an oxygen content of 0.261 wt.%. Notably, the conventional core–rim structure was not dominant in the cermets obtained from the prepared Co- and Ni-coated (Ti,W,Mo,Ta)(C,N) powders. Moreover, the heterogeneous segregation effect of the Co/Ni coating on the ultrafine powder particles resulted in a finer microstructure than the traditional cermets with the same composition. However, the grain size is mainly in the range of 0.5–0.8 μm. The weaker residual stresses at the core and rim interfaces and the finer particle distributions could theoretically enhance the toughness of Ti(C,N)-based cermets, simultaneously.

Porous Titanium Carbide Ceramics Fabricated by Coat-Mix Process

Fabrication of Fully Dense Tial-Based Composite Sheets with A Novel Microlaminated Microstructure

Microstructure, Mechanical Property and Thermal Conductivity of Porous TiCO Ceramic Fabricated by In Situ Carbothermal Reduction of Phenolic Resin and Titania

Microstructure Evolution Process of Porous Silicon Carbide Ceramics Prepared Through Coat-Mix Method

Preparation and Sinterability of Submicron Titanium Carbide Powders Synthesized with Phenolic Resin As Carbon Source by Carbothermal Reduction

Formation Mechanism of Porous Silicon Carbide Ceramic Synthesized by Coat-Mix Process

Preparation and Properties of Porous Silicon Carbide Ceramics Through Coat-Mix and Composite Additives Process

Fabrication and Properties of Ti<sub>3</sub>AlC<sub>2</sub>-Based Ceramics by Two-Step Method

Preparation of Titanium Carbide by Carburisation of Titanium Dioxide

Fabrication and properties of Ti3AlC2-based ceramics by two-step method

DENSE TiC-Al2O3-Fe CERMET FABRICATED BY SHS

Effects of pore microstructures on thermal and mechanical properties of porous TiC fabricated by hot press sintering

Ordered Mesoporous Nanocrystalline Titanium‐Carbide/Carbon Composites from in Situ Carbothermal Reduction

Freeform Fabrication of Ti3SiC2 Powder-Based Structures

Synthesis of ordered mesoporous crystalline carbon-anatase composites with high titania contents.

Fabrication of Porous Al2TiO5-Al2O3 Ceramics Using Al2O3 Hollow Spheres Coated with TiO2 Sol

One-Step Approach for the Fabrication and Characterization of Hydroxyapatite/Tio2 Composite Ceramic Coatings by Micro-Arc Oxidation in Situ on the Surface of Pure Titanium

Preparation and Wear Resistance of Porous TC4 Titanium Alloy Micro‐arc Oxidation Coating Produced by Selective Laser Melting

Fabrication of Composite Coating Particles with Mullite Stoichiometric Ratio by a Novel Processing

The Preparation Process, Microstructure and Properties of Cellular TiC-High Mn Steel-Bonded Carbide

Preparation of Ultrafine Co- and Ni-Coated (Ti,W,Mo,Ta)(C,N) Powders and Their Influence on the Microstructure of Ti(C,N)-Based Cermets