Tailoring porosity and pore size in silicon carbide ceramics with C/SiO2 additions
Kexin Yin,Wenyue Sun,Menghuan Yi,Pu Hu,Zhiliang Huang,Changlian Chen
DOI: https://doi.org/10.1111/ijac.15018
2024-12-17
International Journal of Applied Ceramic Technology
Abstract:Porous silicon carbide ceramics are ideal candidates for filters, separation membranes, and high‐temperature structural materials, for which high porosity and precise pore size control are required. However, high porosity and large pore sizes usually lead to degradation in mechanical properties. In this work, silicon carbide powder with two different particle sizes was used as the raw material, and C powder and SiO2 powder were used as pore‐forming agents. A series of pure silicon carbide porous ceramics with micron‐sized pores were prepared by recrystallization sintering. The porosity and pore size of obtained samples were controllable and adjustable, and the mechanical properties were significantly enhanced. The microstructure, pore size distribution, porosity, and crystal phase of silicon carbide porous ceramics were characterized by scanning electron microscope, pore size analyzer, Archimedes method, and X‐ray diffraction. The effect of adding C/SiO2 on the porosity, the pore size, and the micro‐morphology of sintering samples was studied. The results show that C/SiO2 can adjust the porosity and pore size of pure silicon carbide porous ceramics in a wide range. The highest porosity of the obtained sample adding 40% C/SiO2 was up to 64.42%, and the average and maximum aperture are 5.42 and 11.98 μm, respectively.
materials science, ceramics