Preparation of Titanium Carbide by Carburisation of Titanium Dioxide

Tingting Lv,Fang Tian,Tu Hu

DOI: https://doi.org/10.3390/pr12010102

IF: 3.5

2024-01-01

Processes

Abstract:Titanium carbide has attracted widespread attention due to its excellent properties. This study investigates the process of carbon thermally reducing TiO2 to prepare TiC through a combination of thermodynamic analysis and experiments. The effects of temperature, TiO2/C molar ratio, and time on the phase transformation and morphology evolution of the products are investigated. The synthesis of titanium carbide involves the main reduction path of TiO2–Magnéli–Ti3O5–Ti2O3–TiCxO1−x. With the increase in reaction temperature and TiC content, the microstructure transitions from a smooth disc-like structure to a loose and porous layered structure, while the particle size decreases significantly. The carburisation rate of the reduced product is more affected by temperature, according to chemical analysis. The carburisation rate increased from 18.37% to 36.09% for 2 h–10 h of holding time at 1400 °C, and from 51.43% to 77.57% for 2 h–10 h of holding time at 1500 °C. The quantification of the carburisation rate provides a valuable reference for the preparation of titanium carbide by TiO2.

engineering, chemical

What problem does this paper attempt to address?

### Problems the Paper Aims to Solve

This paper aims to study the process of preparing titanium carbide (TiC) through carbothermal reduction of titanium dioxide (TiO₂). Specifically, the authors combine thermodynamic analysis and experimental methods to explore the effects of temperature, TiO₂/C molar ratio, and reaction time on the phase transformation and morphology evolution of the products.

### Main Research Content

1. **Thermodynamic Calculations**:
- Thermodynamic analysis was conducted using Factsage software to predict the reaction pathways under different conditions.
- The study found that when the TiO₂/C molar ratio is 1:3 and the temperature is 1400℃, TiO₂ can be completely converted to TiC.

2. **Effect of Temperature**:
- At 1300℃, TiO₂ was not completely reduced; signs of carbide formation were observed at 1400℃.
- As the temperature increased from 1300℃ to 1500℃, the diffraction peaks of carbides intensified, indicating that higher temperatures favor an increased rate of carburization.

3. **Effect of Carbon Content**:
- The effect of carbon content on the products was studied at 1500℃ with a holding time of 10 hours under different molar ratios.
- When the TiO₂/C molar ratio was 1:3, TiC was the main product; further increasing the carbon content led to the presence of excess carbon, resulting in waste.

4. **Effect of Holding Time**:
- The effect of different holding times on the products was studied at 1500℃ with a TiO₂/C molar ratio of 1:3.
- Results showed that the carburization rate was faster within 2 to 6 hours; after 8 to 12 hours, the reaction rate decreased due to the reduction in carbon content.

5. **Calculation of Carburization Rate**:
- The carburization rate was calculated based on the total titanium content and titanium carbide content in the products to evaluate the degree of carburization.

Through the above research, the authors hope to find the optimal reaction conditions to achieve efficient preparation of high-purity titanium carbide.