Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Synthesis of TiO(2) Supported on Activated Carbon by MOCVD: Operation Parameters Study.

Preparation of an Ag–TiO2 photocatalyst coated on activated carbon by MOCVD

Preparation of photocatalytic TiO2 coatings of nanosized particles on activated carbon by AP-MOCVD

Preparation of heterogeneous photocatalyst (TiO2/Alumina) by metallo-organic chemical vapor deposition

TiO2 Photocatalyst Deposition by MOCVD on Activated Carbon

Preparation of Heterogeneous Photocatalyst (TiO<sub>2</sub>/Alumina) by Metallo-Organic Chemical Vapor Deposition

Enhancing the Concentration of TiO2 Photocatalyst on the External Surface of Activated Carbon by MOCVD

Preparation of anatase TiO2 supported on alumina by different metal organic chemical vapor deposition methods

Role of carbon in titania as visible-light photocatalyst prepared by flat-flame chemical vapor condensation method

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Low-temperature Preparation and Microwave Photocatalytic Activity Study of TiO2-mounted Activated Carbon.

Study on preparation of TiO_2 loaded on activated carbon and photocatalytic properties

Coating of anatase titania on clinoptilolite by metal organic chemical vapor deposition method: enhanced mesoporosity and photocatalytic activity

A novel approach towards high-performance composite photocatalyst of TiO2 deposited on activated carbon

Effect of preparation methods on the structure and catalytic performance of TiO2/AC photocatalysts

Preparation of Titanium Carbide by Carburisation of Titanium Dioxide

Stabilization of Titanium Dioxide Nanoparticles at the Surface of Carbon Nanomaterials Promoted by Microwave Heating.

Carbon-Deposited TiO<sub>2</sub>: Synthesis, Characterization, and Visible Photocatalytic Performance

One Step Preparation of Visible-Light Responsive Fe–TiO2 Coating Photocatalysts by MOCVD

Visible-light deposition of CrO cocatalyst on TiO2: Cr valence regulation for superior photocatalytic CO2 reduction to CH4

Preparation of Nano-Sized TiO2 Supported on Granular Activated Carbon and the Photocatalytic Degradation of Methylene Blue