Abstract:Amorphous alumina films are isotropic and have no grain boundaries, which make them have smooth surfaces, excellent properties, and wide applications in protective coatings, catalysis, and microelectronics. However, high-quality alumina films were usually prepared by vapor-phase approaches which need expensive equipment and long production time. Additionally, amorphous films are long-range disordered, which makes the study of structure–property relationships challenging. Here, a simple sol–gel method is employed to obtain high-quality amorphous Al2O3 thin films. The microstructure, morphology, and mechanical properties of amorphous Al2O3 thin films were systematically investigated. All the Al2O3 thin films heat-treated at 600–800∘C are in amorphous state with ultrasmooth surface (Ra values about 0.29–0.43 nm) and high mechanical properties (elastic modulus ∼170[Formula: see text]GPa, hardness ∼20[Formula: see text]GPa). The mechanical properties (E and H) of Al2O3 films gradually increase with the increase of heat-treating temperature. Additionally, the Al coordination of the amorphous alumina films are analyzed by solid-state NMR and correlated with the mechanical properties. The results show that in amorphous alumina, the presence of tetrahedral Al ([4]Al) and octahedral Al ([6]Al) is helpful to improve the mechanical properties, while the five-coordinated Al ([5]Al) is not conducive to improve the mechanical properties. The results demonstrate that sol–gel method is an attractive alternative to time-consuming and expensive vapor-phase approaches and are useful for scale-up to applications and research of amorphous alumina films.

Low-temperature Non-hydrolytic Sol-gel Synthesis of Aluminum Titanate

In-Situ Anatase Flake Crystals Prepared By Sol-Gel Method At Low Temperature

Sol–gel Synthesis and Sintering of Nano-Size Li2TiO3 Powder

The Characterization and Preparation of Nano-Scale Fe Doping Tio2 by Sol-Gel Method (I) - the Crystallization and Thermal Decomposition Process of Fe Doping Tio2 Xerogel Powders Using Thermal Tg-Ir Spectrometry

Low-Temperature Preparation of Ag-TiO2 Composite Films and Their Properties

Preparation and Heat Treatment of Titania Aerogels by Ambient Pressure Drying

Effects of Heat-Treatment Temperature on Preparation of the Sol-Gel-Derived Ag/TiO2 Films

Sol-Gel Preparation of N-doped TiO2 Nanocrystalline at Low Temperature

Facile synthesis of nano-crystalline alpha-alumina at low temperature via an absolute ethanol sol-gel strategy

Preparation of TiO2 films under low temperature condition on the glass substrate

Low-temperature Synthesis of Nano-Crystalline Magnesium Titanate Materials by the Sol–gel Method

Preparation of Monolithic Aluminium Titanate with Well-Defined Macropores Via a Sol–gel Process Accompanied by Phase Separation

Preparation of Ti1-xFexO2 Nanocrystals via Low Temperature Sol-Gel Method

Effects of Water Amount and Ph on the Crystal Behavior of a TiO2 Nanocrystalline Derived from a Sol–Gel Process at a Low Temperature

The Microstructure, Morphology, and Mechanical Properties of Sol-Gel-derived Amorphous Aluminum Oxide Films

Structure ,thermal Expansion and Thermal Stability of Aluminium Titanate Materials

PREPARATION AND PROPERTIES OF ALUMINUM TITANATE SOLID SOLUTION CERAMICS

Formation and transformation of ZnTiO3 prepared by sol–gel process

Effects of process parameters on nonhydrolytic sol-gel synthesis of Ba0.6Sr0.4TiO3 powders

Synthesis of Aluminum Titanate Solid Solution by Solid State Reaction of Fine Commercial Al2o3, Tio2 and Mgo Powders

Gelation and heat treatment of preparing BaNd2Ti5O14 with autocombustion methods