Abstract:Fully dense ceramics with retarded grain growth can be attained effectively at relatively low temperatures using a high-pressure sintering method. However, there is a paucity of in-depth research on the densification mechanism, grain growth process, grain boundary characterization, and residual stress. Using a strong, reliable die made from a carbon-fiber-reinforced carbon (Cf/C) composite for spark plasma sintering, two kinds of commercially pure α-Al2O3 powders, with average particle sizes of 220 nm and 3 μm, were sintered at relatively low temperatures and under high pressures of up to 200 MPa. The sintering densification temperature and the starting threshold temperature of grain growth (Tsg) were determined by the applied pressure and the surface energy relative to grain size, as they were both observed to increase with grain size and to decrease with applied pressure. Densification with limited grain coarsening occurred under an applied pressure of 200 MPa at 1050 °C for the 220 nm Al2O3 powder and 1400 °C for the 3 μm Al2O3 powder. The grain boundary energy, residual stress, and dislocation density of the ceramics sintered under high pressure and low temperature were higher than those of the samples sintered without additional pressure. Plastic deformation occurring at the contact area of the adjacent particles was proved to be the dominant mechanism for sintering under high pressure, and a mathematical model based on the plasticity mechanics and close packing of equal spheres was established. Based on the mathematical model, the predicted relative density of an Al2O3 compact can reach ∼80 % via the plastic deformation mechanism, which fits well with experimental observations. The densification kinetics were investigated from the sintering parameters, i.e., the holding temperature, dwell time, and applied pressure. Diffusion, grain boundary sliding, and dislocation motion were assistant mechanisms in the final stage of sintering, as indicated by the stress exponent and the microstructural evolution. During the sintering of the 220 nm alumina at 1125 °C and 100 MPa, the deformation tends to increase defects and vacancies generation, both of which accelerate lattice diffusion and thus enhance grain growth.

Low-temperature Sintering of A1N Ceramics with Shock Wave Treated Powder

Characterization of shock waves treated aluminum nitride powder and its potential for low-temperature sintering

Optimization of Microstructure to Improve Si3n4 Ceramics with Thermal Conductivity and Mechanical Properties: Effect of Si and Α-Si3n4 Powder Composition

High-pressure Synthesis of High-Performance Submicron-Sized Polycrystalline Β-Si3n4 Bulk Without Additives

Raction synthesis of Y2O3/A1N ceramic and mechanism of densification

Sintering of c-BC2N, Solid Solutions of Metallic Phases Particles with the Additives of Oxide Components and NiCr at Ultra-High Load and Temperature of Spark-Plasma Sintering, High Compaction Pressure During the Explosive Method

Incorporation of Metallic Components Into a Structure of Titanium Carbonitride at Ultra-High Load and Temperature of Spark Plasma Sintering and at Different Compaction Pressures During Explosive Method

Preparation of SiC-AlN Ceramic Alloy Powder by Direct Reaction Between Constituent Elements and Property Evaluation of Its Sintered Compacts.

Low temperature fabrication of highly dense α‐Si3N4 ceramics

Densification mechanism and microstructure characteristics of nano- and micro- crystalline alumina by high-pressure and low temperature sintering

Realizing near-full density monophasic tetragonal 1.5-mol% yttria-stabilized zirconia ceramics via current-ramp flash sintering

Structure and Properties of Aln Ceramics Prepared with Spark Plasma Sintering of Ultra-Fine Powders

RESEARCH ON THE REACTION SYNTHESIS OF AlN-BASED CERAMICS WITH THE ADDITION OF Y2O3

Low-temperature sintering of Al2O3 ceramics doped with 4CuO-TiO2-2Nb2O5 composite oxide sintering aid

Microstructure of low-temperature sintered AlN

Low-Temperature Sintering of Bi(Ni0.5Ti0.5)O3-BiFeO3-Pb(Zr0.5Ti0.5)O3 Ceramics and Their Performance

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

Aluminum nitride‐based ceramics with excellent thermal shock resistances

Effect of Heating Rate on Spark Plasma Sintering of a Nanosized Β-Si3n4-based Powder

Densification and Enhancement of Sic Particulate Reinforced Fine Grain Sic Ceramic

Low-temperature synthesis of K0.5Na0.5NbO3 ceramics in a wide temperature window via cold-sintering assisted sintering method and enhanced electrical properties