Abstract:Fully dense ceramics with retarded grain growth can be attained effectively at relatively low temperatures using a high-pressure sintering method. However, there is a paucity of in-depth research on the densification mechanism, grain growth process, grain boundary characterization, and residual stress. Using a strong, reliable die made from a carbon-fiber-reinforced carbon (Cf/C) composite for spark plasma sintering, two kinds of commercially pure α-Al2O3 powders, with average particle sizes of 220 nm and 3 μm, were sintered at relatively low temperatures and under high pressures of up to 200 MPa. The sintering densification temperature and the starting threshold temperature of grain growth (Tsg) were determined by the applied pressure and the surface energy relative to grain size, as they were both observed to increase with grain size and to decrease with applied pressure. Densification with limited grain coarsening occurred under an applied pressure of 200 MPa at 1050 °C for the 220 nm Al2O3 powder and 1400 °C for the 3 μm Al2O3 powder. The grain boundary energy, residual stress, and dislocation density of the ceramics sintered under high pressure and low temperature were higher than those of the samples sintered without additional pressure. Plastic deformation occurring at the contact area of the adjacent particles was proved to be the dominant mechanism for sintering under high pressure, and a mathematical model based on the plasticity mechanics and close packing of equal spheres was established. Based on the mathematical model, the predicted relative density of an Al2O3 compact can reach ∼80 % via the plastic deformation mechanism, which fits well with experimental observations. The densification kinetics were investigated from the sintering parameters, i.e., the holding temperature, dwell time, and applied pressure. Diffusion, grain boundary sliding, and dislocation motion were assistant mechanisms in the final stage of sintering, as indicated by the stress exponent and the microstructural evolution. During the sintering of the 220 nm alumina at 1125 °C and 100 MPa, the deformation tends to increase defects and vacancies generation, both of which accelerate lattice diffusion and thus enhance grain growth.

Characterization of shock waves treated aluminum nitride powder and its potential for low-temperature sintering

Low-temperature Sintering of A1N Ceramics with Shock Wave Treated Powder

Structure and Properties of Aln Ceramics Prepared with Spark Plasma Sintering of Ultra-Fine Powders

Enhanced thermal shock resistance of BN-based composites sintered by hot-pressing with the introduction of nano oxides

Synthesis of Aluminum Nitride Powders from A Plasma-Assisted Ball Milled Precursor Through Carbothermal Reaction

Structure and thermal conductivity of powder injection molded AlN ceramic

Effect of powders on aluminum nitride components fabricated by PIM

Ultrafast high-temperature sintering of aluminum nitride

Vibration Assisted Hot‐Press Sintering of AlN Ceramics

Preparation of AlN Powder of Low Oxygen Content Via Carbothermal Reduction and Nitridation by Active Gas Exchange Technique

Microstructure of low-temperature sintered AlN

Hydrothermal-carbothermal synthesis of highly sinterable AlN nanopowders

Hydrolysis control of AlN powders for the aqueous processing of spherical AlN granules

Strengthening Mechanism of Aluminum Nitride Ceramics from 293 to 77 K

Non hydrolizable aluminum nitride powders surface modified by silicic acids

High Temperature Deformation of Ain

Densification mechanism and microstructure characteristics of nano- and micro- crystalline alumina by high-pressure and low temperature sintering

SPARK PLASMA SINTERING OF AlN POWDERS OBTAINED FROM COMBUSTION SYNTHESIS AND THEIR THERMAL CONDUCTIVITY

Aluminum nitride‐based ceramics with excellent thermal shock resistances

Synthesis of nearly spherical AlN particles by an in-situ nitriding combustion route

Migration of Liquid Phase and Grain Growth in Low-Temperature Sintering of AlN