Abstract:The hot deformation characteristics. of as-cast nickel-base superalloy GH742y after hot isostatic pressing (HIP)(hereafter referred to as-cast alloy) have been investigated by hot compression tests in the temperature range of 1050 to 1140 degrees C, strain rate range of 0.01 s(-1) to 10 s(-1) and strain range of 35% to 50% by means of Gleeble-3500 thermal mechanical simulator. The results show that the as-cast alloy exhibits the poor deformability,and shows wedge-shaped cracking beyond the strain of 35%. At strain rates less than 1.0 s(-1), the stress-strain curves exhibit nearly steady-state behavior, while at strain rate of 10 s(-1), a yield drop and serrated yielding occur. The activation energy values developed on the basis of the experimental data are divided into three domains. The first domain appears at lower strain rate (<= 1.0 s(-1)) and lower temperature (<= 1080 degrees C), with the lowest mean value of activation energy about 261.4 kJ/mol. The second domain appears at the same strain rate as the first domain, but higher temperature (>1080 degrees C), with the intermediate mean value of activation energy about 328.8 kJ/mol. The third domain appears at higher strain rate (10 s(-1)) and temperature range of 1050 to 1140 degrees C, with the largest mean value of activation energy about 605.05 kJ/mol. Three different constitutive equations are established in corresponding to domains. Microstructural observations in the third domain reveal non-uniform dynamic recrystallization (DRX) of homogeneous gamma phase, which leads to the poor deformability and the highest Q value. In contrast, microstructures in the first domain show fully DRX of homogeneous gamma phase, leading to the better deformability and the lowest Q value. It is noted that the grain size increases with the increment of strain rate or temperature. These results suggest that bulk metal working of this material may be carried out in the first domain where fully DRX of gamma homogeneous occurred.

High Temperature Deformation of Ain

Plastic Deformation and Sintering of Alumina under High Pressure

High-temperature Deformation Behavior of SiC-AlN Ceramic Alloys with Fine-grained Microstructure.

High-Temperature Strength of Sic-Aln Solid-Solutions and Composites As Evaluated by Small Punch Tests

Pressureless Sintering and High-Temperature Strength of SiC-AlN Ceramics

Mechanical Properties of AlN-SiC Ceramic Composites Synthesized by Pressureless Sintering and Post-HIP Treatment.

The Deformation Behavior and Microstructure Evolution of a Mn- and Cr-Containing Al-Mg-Si-Cu Alloy During Hot Compression and Subsequent Heat Treatment

The Hot Deformation Behavior and Processing Map of Powder Metallurgy Nial-Based Alloy

Hot Deformation Characteristics for a Nickel-base Superalloy GH742y

Hot Workability and Superplasticity of Low-Al and High-Nb Containing TiAl Alloys

Characterization of shock waves treated aluminum nitride powder and its potential for low-temperature sintering

High temperature deformation mechanism and microstructural evolution of relatively lightweight AlCoCrFeNi high entropy alloy

THE SUPERPLASTICITY OF Fe-28Al-5Cr AND Fe-28Al-5Cr-0.5Nb-0.1C ALLOYS

Deformation Behavior and Constitutive Model for High Temperature Compression of a Newly Type of Ni3Al‐based Superalloy

Property characteristics of a AlNp/Al composite fabricated by squeeze casting technology

Hot Deformation Characteristics of Ti43.5Al5Nb1V1Y Alloy by Hot Press Sintering

Deformation Behavior and Microstructural Evolution of Inconel 625 Superalloy during the Hot Compression Process

Microstructure and Mechanical Properties Determined in Compressive Tests of Quasi-Rapidly Solidified NiAl-Cr(Mo)-Hf Eutectic Alloy after Hot Isostatic Pressure and High Temperature Treatments

High Temperature Tensile and Compressive Behaviors of Nanostructured Polycrystalline AlCoCrFeNi High Entropy Alloy: A Molecular Dynamics Study

Hot deformation behavior of novel high-strength Mg-0.6Mn-0.5Al-0.5Zn-0.4Ca alloy

Thermal Deformation Behavior of Novel Ni-Based PM Superalloy Under Different Initial Conditions