Investigation on the microstructure evolution and dynamic recrystallization mechanisms of TiAl alloy at elevated temperature
Shiwei Tian,Anrui He,Jianhua Liu,Yefei Zhang,Siyuan Zhang,Yun Zhang,Yonggang Yang,Haitao Jiang
DOI: https://doi.org/10.1016/j.jmrt.2021.06.107
IF: 6.267
2021-09-01
Journal of Materials Research and Technology
Abstract:<p>The flow stress-strain curves appear to be sensitive to deformation conditions. The ratio of critical strain to peak strain <em>ε</em><sub><em>c</em></sub><em>/ε</em><sub><em>p</em></sub> follows a linear relationship except when the temperature is 1240 °C and the strain rate is 0.001 s<sup>-1</sup>. During the deformation, the fragmentation and decomposition of γ/α<sub>2</sub> lamellae are related to recrystallization of α<sub>2</sub> and γ laths in the lamellae and the γ→α<sub>2</sub> phase transformation, the former depends on dislocation slip and twinning, and the latter is related to temperature, local stress concentration and diffusion time. As for the recrystallization mechanisms, the γ phase is discontinuous dynamic recrystallization (DDRX) mode, while the α<sub>2</sub> phase relies on continuous dynamic recrystallization (CDRX) mode. The β phase has more low-angle grain boundaries (LAGB) during deformation, indicating the continuous coordinated deformation, and this explains the enlarged hot working window of the TiAl alloy (1165∼1240°C/0.001∼1s<sup>-1</sup> and 1120∼1165 °C/0.001∼0.4 s<sup>-1</sup>).</p>
materials science, multidisciplinary,metallurgy & metallurgical engineering