High-temperature hot deformation behavior and processing map of Ti-22Al-25Nb alloy

Yunpeng Chai,Yanchun Zhu,Ling Qin,Yuanyuan Luo,Yong Niu,Zhucai Shao
DOI: https://doi.org/10.1016/j.mtcomm.2024.110599
IF: 3.8
2024-10-06
Materials Today Communications
Abstract:The high-temperature deformation behavior of the Ti-22Al-25Nb alloy was investigated by conducting hot compression experiments. A constitutive equation predicting the flow behavior of the Ti-22Al-25Nb alloy was established by analyzing its stress–strain curves. The strain-compensated constitutive equation effectively predicted the flow stress of the alloy with a correlation coefficient of 0.992 between the measured and predicted values and an average absolute relative error of 6.548 %. A hot processing map was obtained based on a dynamic material model. It demonstrated that the optimal processing region corresponded to the deformation temperatures of 1273–1353 K and strain rates of 0.001–0.01 s −1 . Using electron backscatter diffraction data, thermal deformation mechanisms were elucidated under different deformation conditions within the safe region. The obtained results revealed that under the low temperature ( T ≤ 1323 K) and low strain rate ( ε̇ ≤ 1 s −1 ) conditions, continuous dynamic recrystallization and dynamic recovery (DRV) were the main thermal deformation mechanisms. Under the medium-to-high temperature ( T ≥ 1323 K) and low strain rate ( ε̇ ≤ 1 s −1 ) conditions, the main thermal deformation mechanisms were discontinuous dynamic recrystallization and DRV. At high strain rates ( ε̇ ≥ 1 s −1 ), the primary thermaldeformation mechanism was DRV. The occurrence of discontinuous yielding in the alloy at high strain rates was related to the proliferation of mobile dislocations at grain boundaries.
materials science, multidisciplinary
What problem does this paper attempt to address?