Optimizing AlN hydrolysis process to fabricate coated modified powders for improving the properties of Si 3 N 4 /SiAlON ceramics prepared by Vat Photopolymerization
Wei-Kang Li,Ren-Zhong Zhang,Jia-Min Wu,Lin Guo,Wei-Hao Cai,Xin Lin,Hai-Sheng Xu,Fen Wang,Yu-Sheng Shi
DOI: https://doi.org/10.1016/j.addma.2024.104460
IF: 11
2024-09-29
Additive Manufacturing
Abstract:The preparation of complex structural parts of Si 3 N 4 and its composite ceramics using conventional methods is difficult. The Vat Photopolymerization (VPP) technique is regarded as an effective method for the preparation of ceramic materials. However, due to the high absorption of ultraviolet (UV) light and high refractive index of Si 3 N 4 , it is challenging to realize its complex structure via VPP technique. AlN and Si 3 N 4 can be compounded to form SiAlON phase, and AlN powders can be hydrolyzed to produce Al(OH) 3 that can be easily dehydrated. In this study, Si 3 N 4 @Al 2 O 3 and AlN@Al 2 O 3 powders were prepared by mixing Si 3 N 4 and AlN powders by hydrolysis. Subsequently, Si 3 N 4 /SiAlON composite ceramics were prepared by VPP. With the addition of 10 vol% AlN, the viscosity of ceramic slurry was found to be 0.50 Pa·s. Furthermore, the curing depth was observed to reach 49.46 ± 2.15 μm at 800 mJ/cm 2 . The sintered ceramics exhibited the formation of the excellent β-Si 3 N 4 /β-SiAlON phase. The relative density, bending strength, hardness, fracture toughness and thermal conductivity was determined to be 92.61 ± 2.51%, 402.91 ± 9.61 MPa, 21.11 ± 0.61 GPa, 6.33 ± 0.25 MPa· m12 and 33.17 ± 1.01 W·m -1 ·K -1 , respectively. This study introduces a novel approach to cladding modification of Si 3 N 4 and AlN, as well as the preparation of Si 3 N 4 /SiAlON composite ceramics with exceptional properties via VPP.
engineering, manufacturing,materials science, multidisciplinary