Abstract:Aluminium nitride (AlN) is an important technical ceramic with outstanding strength and thermal conductivity that has important applications for advanced heat sink materials and as a reinforcement for metal-based composites. In this study, we report a novel, straightforward and low-cost method to prepare AlN powder using a vacuum tube furnace for the direct nitridation of loose aluminium powder at low temperatures (down to 500 ∘C) under flowing high-purity nitrogen. Small amounts of magnesium powder (1 wt.%), combined with aluminium, promote nitridation. Here, we characterise the effects of time (up to 12 h) and temperature (490 to 560 ∘C) on nitridation with the aim to establish an effective regimen for the controlled synthesis of an aluminium nitride reinforcement powder for the production of metal matrix composites. The extent of nitridation and the morphology of the reaction products were assessed using scanning electron microscopy and X-ray diffraction analyses. AlN was detected for all nitriding temperatures ≥ 500 ∘C, with the highest yields of 80% to 85% obtained at 530 ∘C for times ≥ 1 h. At this temperature, nitridation proceeded rapidly, and there was extensive agglomeration of the reaction products making it difficult to reprocess into powder. At lower temperatures around 510 ∘C, a relatively high proportion of AlN was attained (>73% after 6 h) while retaining excellent friability so that it could be manually reprocessed to powder. The synthesised reinforcement consisted of micro- or nano-crystalline AlN comingled with metallic aluminium. The ratio of AlN and metallic aluminium can be readily controlled by varying the nitriding temperature. This provides a flexible and accessible method for the production of AlN-reinforcement powders suited to the production of metal matrix composites.

Aluminum nitride nanoparticles with high purity prepared via urea glass route under different sintering conditions

Facile synthesis of monodisperse aluminum nitride microspheres

Hydrothermal-carbothermal synthesis of highly sinterable AlN nanopowders

Synthesis of AlN nanocrystalline powders

High-performance aluminum nitride made by Vat photopolymerization through optimization of resin refractive index and plasticizer content

Impact of Various Input Parameters on the Preparation of Different AlN Nanostructures by Hybrid Route of Hydrothermal and Carbothermal Reduction Nitridation Technique

High purity and good dispersity AlN nanoparticles synthesized by an arc discharge with assistance of direct nitridation

Synthesis of aluminum nitride by nitridation of γ-Al 2O3 nanopartlcles in flowing ammonia

Non hydrolizable aluminum nitride powders surface modified by silicic acids

Synthesis of Aluminum Nitride Using Sodium Aluminate as Aluminum Source

Synthesis of nearly spherical AlN particles by an in-situ nitriding combustion route

High-Thermal-Conductivity AlN Ceramics Prepared from Octyltrichlorosilane-Modified AlN Powder

Impacts of Temperature and Time on Direct Nitridation of Aluminium Powders for Preparation of AlN Reinforcement

Some properties of aluminium-nitride powder prepared by metal-organic chemical vapour deposition

The Durability of Various Crucible Materials for Aluminum Nitride Crystal Growth by Sublimation

Nanosized Aluminum Nitride Hollow Spheres Formed Through a Self-Templating Solid–gas Interface Reaction

Synthesis of Aluminum Nitride by Nitridation of γ-Al<sub>2</sub>O<sub>3</sub> Nanoparticles in Flowing Ammonia

Preparation of Aln Films by Pulsed Laser Deposition Using Sintered Aluminum Nitride and Elemental Aluminum As Raw Materials

Fabrication of High Thermal Conductivity Aluminum Nitride Ceramics via Digital Light Processing 3D Printing

Synthesis of Aluminum Nitride by Nitridation of Γ-Al2o3 Nanoparticles in Flowing Ammonia