Abstract:In the present paper, the NiAl based composite strengthened by TiC and ZrO2 ceramic particles (NiAl-TiC-ZrO2 for short) was prepared by the hot press aiding exothermic synthesis (HPES) technique to get a material with good wear properties. OM, SEM and TEM were employed to investigate the microstructure of the NiAl-TiC-ZrO2 composite. The mechanical properties and wear behaviour were studied by compression and dry sliding wear tests. The results showed that the NiAl-TiC-ZrO2 composite possesses fine microstructure, but the TiC and ZrO2 particles tended to agglomerate along NiAl phase boundary. Further observations revealed that the ultrafine ZrO2 particles contained stacking faults and microtwins inside and thin amorphous layer was generated along some interfaces of NiAl and TiC phases. Compression tests exhibited that the addition of TiC and ZrO2 particles could increase the strength of the NiAl-TiC-ZrO2 composite significantly. Wear tests results demonstrated that the NiAl-TiC-ZrO2 composite had relative good wear resistance at high temperature. Especially at 973 and 1073 K, the composite exhibited selflubrication behaviour, which might be attributed to the lubricant film formed on the worn surface. TEM observation on the lubricant film revealed that it was composed of amorphous matrix and nanoparticles. Moreover, TEM observation found the composite near the worn surface contained ultrafine microstructure. When the temperature increased or decreased, the lubricant film would be spalled partly, which led to the increasing of the friction coefficient and wear rate.

Contributions of the Particulate Reinforcement to Dry Sliding Wear Resistance of Rapidly Solidified Al-Ti Alloys

Dry sliding wear of MA/PM Al-10Ti alloy

Effects of second phase on dry sliding wear of rapidly solidified Al-Ti alloy

Thermal stability and its effects on the mechanical properties of rapidly solidified Al-Ti alloys

Dry sliding wear of PM Al-10Ti alloy

Microstructure and Sliding Wear Behavior of PM Alloy Al10Ti after Thermal Exposure

Mechanical properties of rapidly solidified Al-Ti alloys after thermal exposure

Effect of TiC-particle Size on Sliding Wear of TiC Particulate Reinforced Alumina Composites

Preparation of Ultra-Fine ATC Ceramics and Analysis of Its Dry-Sliding Wear Behavior

Effect of Cold Deformation on Low Speed Sliding Wear of Al-10Ti Alloy

Importance of Al2TiO5 particle on the mechanical and wear performance of stir cast AA6061 composite using Central Composite Design

Enhancing microstructural, tribological and corrosion responses of Al–Zn–Mg–Cu alloy via nano-/micro-Al2O3 particulates

Wear-resistance mechanism of an Al–12Si alloy reinforced with aluminosilicate short fibers

Effects of silicon content and test conditions on the dry wear behaviour of Zn–30Al–3Cu–(0–5)Si Alloys

Surface Wear Behavior and Strengthening Mechanism of Al3Zr Particle Reinforced Aluminum Matrix Composites Prepared in Situ

Sliding and Fretting Wear Behavior of Biomedical Ultrafine-Grained TiNbZrTaFe/Si Alloys in Simulated Physiological Solution

Dry sliding wear behavior of additively manufactured CoCrWNixAly alloys

Tribological behavior of aluminum matrix composites reinforced with ceramic particulates in dry sliding against a semimetallic friction material

Dry sliding friction and wear properties of B4C particulate-reinforced Al-5083 matrix composites

Microstructural feature dependence of dry sliding wear behaviors in a γ-TiAl alloy

Microstructure and Wear Behaviour of Ceramic Particles Strengthening Nial Based Composite