Dry Sliding Wear Behavior Of Hot-Dip Aluminized Ti-6al-4v Alloy Against Gcr15 Steel
Chen Wei,Zhang Benguo,Jiang Wei,Cui Xianghong,Wang Shuqi
2019-01-01
Rare Metal Materials and Engineering
Abstract:An aluminized coating of TiAl3 was prepared on Ti-6Al-4V alloy by hot-dip aluminizing (HDA) and subsequent high-temperature diffusion at 650 degrees C. Dry sliding wear behavior for the aluminized Ti-6Al-4V alloy against GCr15 steel was investigated by a pin-on-disc wear tester. The morphology, phase and composition of worn surface of the HDA coatings were characterized by SEM, XRD, EDS and XPS. The wear mechanism was also explored. The result demonstrates that with an increase of sliding velocity, the wear loss of the aluminized Ti-6Al-4V alloy decreases to a lower value at 0.75 m/s, then increases to the highest value at 2.68 m/s, and finally decreases to the lowest at 4 m/s. At different sliding velocities, the wear loss increases with the increase of load. Tribo-layers notably affect the wear behavior and mechanism. At 4 m/s, oxide-containing tribo-layers (TiO and TiO2) possess an obvious wear-reduced function; conversely, at 2.68 m/s, no-oxide layers show no protection from wear. Compared with uncoated Ti-6Al-4V alloy, the aluminized coating improves the wear resistance of the titanium alloy under various conditions, especially 4 m/s. The improved wear performance is attributed to Ti-Al coating and tribo-oxide layer.