Abstract:In this study, the in-situ ZrB 2 /Al-Si5Cu3 aluminum alloy composites were fabricated through the salt-melt reaction route with different weight fractions of ZrB 2 reinforcements, i.e., 2.5%, 5%, and 7.5%. The composites were tested for their density, hardness, tensile strength, flexural strength, impact strength, and wear properties. The influence of reinforcement on the properties was studied concerning the wt.% of reinforcement. The increase in density of composites compared to the matrix material confirms the formation of the in-situ reinforcement phase. The microstructure showed a desirable distribution of reinforced particles over the matrix at all weight fractions of the reinforcements in the composites. The ZrB 2 particles formed in the matrix have particle sizes in the range from 255 nm to 955 nm and the grain size has been reduced from 242 microns to 110 microns as the result of particle-induced solidification. The hardness of the composites containing ZrB 2 reinforcements of 2.5, 5, and 7.5 wt.% showed improvement by 8%, 17.5%, and 34% respectively compared to the parent alloy. There is an improvement in the tensile strength and elongation for the wt.% of ZrB 2 up to 5 wt.%, from 115 MPa to 183 MPa, after which, there was a drop in the tensile strength. The detailed analysis of tensile fractography shows that the agglomerated ZrB 2 reinforced particles at higher weight fractions lead to a decrease in strength. The results of flexural strength also affirm the strength of 5 wt.% ZrB 2 /Al-Si5Cu3 increased from the matrix material's flexural strength of 337 MPa to 672 MPa. The wear study shows that the composite with 7.5 wt.% ZrB 2 possesses a higher wear resistance. However, the impact strength did not show any differences in the weight % of reinforcement.

Surface Wear Behavior and Strengthening Mechanism of Al3Zr Particle Reinforced Aluminum Matrix Composites Prepared in Situ

Preparation and mechanical and tribological properties of A1(3)Zr+6082Al composites fabricated by magnetic stirring in situ

Preparation and Mechanical and Tribological Properties of A13Zr+6082Al Composites Fabricated by Magnetic Stirring in Situ

Preparation of in-situ ZrB2/A356 composites and high-temperature tribological studies

Fabrication and Dry Sliding Wear Behavior of in Situ Al–K2ZrF6–KBF4 Composites Reinforced by Al3Zr and ZrB2 Particles

Corrosion and wear performance and mechanism study of ZrB2/AA6016

Microstructures and Dry Sliding Wear Properties of in Situ (al3zr+zrb2)/al Composites

Effects of Molten Temperature on the Morphologies of in Situ Al3Zr and ZrB2 Particles and Wear Properties of (al3zr+zrb2)/al Composites

Wear Resistance of Nanometer and Micron Al2O3 Particles Reinforced Aluminum Matrix Hybrid Composites

Contributions of the Particulate Reinforcement to Dry Sliding Wear Resistance of Rapidly Solidified Al-Ti Alloys

The Magnetic Chemical Preparation and Properties of the Al3Zr/6A02 Aluminum Matrix Composites

Microstructures and mechanical properties of aluminum matrix composites fabricated from Al-x wt.% Zr(CO3)2 (x = 5, 10, 15, 20, 25) systems

Three-body Abrasive Wear Resistance of Iron Matrix Composites Reinforced with Ceramic Particles

Mechanical and Wear Properties of Al<sub>2</sub>O<sub>3</sub>-15wt%ZrO<sub>2</sub> Composites

Tribological Properties of in Situ Fe3al-20 Wt% Al2o3 Composites

Dry Sliding Wear of a Ti50Ni25Cu25 Particulate-Reinforced Aluminum Matrix Composite

Mechanical and Wear Behavior of Al-Si5Cu3/ZrB2 In-Situ Reinforced Metal Matrix Composite

Nano-particle Reinforced Magnesium Matrix Composites

Wear Behavior of Al3Ti/Mg Composites

Tribological Behavior of In-Situ (cr, Mo)/Fe3al-20 Wt.%Al2o3 Composites at Elevated Temperatures

Investigation of wear and transverse rupture strength of AA2219/ZrO2/B4C hybrid composite materials prepared with 3D ball mixer and produced by spark plasma sintering