Preparation of Ultra-Fine ATC Ceramics and Analysis of Its Dry-Sliding Wear Behavior

ZHU Liu,LI Jian,LING Guo-ping,WANG You-wen

DOI: https://doi.org/10.3785/j.issn.1008-973x.2005.12.002

2005-01-01

Abstract:To improve the wear resistance and fracture toughness of ceramic-tools material,the ultra-fine Al_2O_3-TiC-8%Co(ATC) ceramics were prepared.Cobalt was coated on the surface of the sub-micron Al_2O_3 and TiC particles by low temperature electroless plating,and then the composite powders were sintered into the ATC samples.The wear resistance of ATC ceramics was investigated by the pin-on-disc wear device,and the worn surface morphologies were examined by scanning electron microscopy(SEM).The results show that the effect of the fracture toughness on the wear resistance of ceramic materials is very obvious and the particle spalling predominates during the dry sliding wear process.With the increasing test time,the worn surface of ATC ceramic becomes smooth and the relative wear rate decreases during the wear processes.Cobalt coated on ultra-fine Al_2O_3 and TiC can depress the grain growth during the sintering process,and consequently improve the fracture toughness and wear resistance of ATC ceramics.