Abstract:A series of alumina-pillared layered tetratitanates with different interlayer spacings (d(001) = 15.2-17.0 Angstrom) has been first prepared through a step-wise exchange process and by finely changing the exchange reaction conditions such as reaction time and molar ratio of reactants in the reaction mixture, and hydrolysis conditions such as the pH and aging time used to generate the pillaring agent. Apart from the interlayer spacing, the pore diameter and specific surface area of the pillared samples can also be changed by varying the preparation conditions. The resulting alumina-pillared layered tetratitanates were porous, with both micro- and meso-pores (average pore diameter=61.5-95.8 Angstrom). The specific surface area (BET, N-2, 77 K) of the starting material K2Ti4O9 (5 m(2) g(-1)) was increased by pillaring up to 56.6-105.6 m(2) g(-1). The relatively high surface area is mainly due to the microporous structure of the interlayered spaces formed by stable alumina pillars. The structure of the alumina-pillared layered tetratitanates was thermostable above 500 degrees C. The results are compared with those previously reported.

Preparation of Silica-Pillared Layered Tetratitanate with a High Surface Area

Highly Thermostable, Porous, Layered Titanoniobate Pillared by Silica

Preparation of Layered Ferrititanate Pillared by Silica

Preparation and characterization of silica-pillared layered titanate

Synthesis and Characterization of Alumina-Pillared Layered Tetratitanates with Different Interlayer Spacings

Preparation and characterization of a silica-pillared layered lanthanum titanate

Synthesis of Porous Chromia-Pillared Tetratitanate

Syntheses and Characterization of Silica - Pillared Layered Ferrititanates

Synthesis of Silica-Pillared Layered Lanthanum Titanate with High Thermal Stability

Preparation and Characterization of Alumina-Pillared Layered Titanate with A High Interlayer Spacing

Synthesis and Characterization of Chromia-Pillared Layered Tetratitanate

Preparation of Novel Mesostructured Titanium-Pillared Hydrotalcite

Preparation of Porous Chromia-Pillared Titanoniobate

SYNTHESIS OF AL2O3-PILLARED LAYERED TITANONIOBATE

Synthesis and characterization of titania-pillared layered HLaNb2O7 with high specific surface area

Synthesis Of Titania-Pillared Layered Niobic Acid With A High Specific Surface Area By Using Sol-Intercalation Method

Atomic layer deposition of TiO2 on mesoporous silica

Preparation of Alumina-pillared Layered Titanoniobates with Different Interlayer Distances

A New Method for Preparing Nickel Oxide Supported Silica Pillared Phosphates with High Surface Area

Synthesis of easily shaped ordered mesoporous titanium-containing silica

Preparation and Catalytic Behaviour of Cr2o3-Pillared Tin Phosphate with High Surface Area