Preparation and Characterization of Alumina-Pillared Layered Titanate with A High Interlayer Spacing

Hou Wenhua,Yan Qijie,Fu Xiancai

DOI: https://doi.org/10.3866/pku.whxb19940202

1994-01-01

Abstract:This note mainly reports a successful preparation of a alumina-pillared layered titanate with a high interlayer spacing through a step wise exchange process. X-ray diffraction patterns indicate that the resultant alumina-pillared layered titanate has interlayer spacing of 1.70 nm, which is 0.17 nm higher than that of previously reported, and has a thermal stability over 500 degrees C. The surface area (N-2,BET method) of the product is determined to be 72.4 m(2) g(-1). The N-2 adsorption and desorption isotherm of the product demonstrates that the resultant alumina-pillared layered titanate is porous, with both micropores and mesopores.