Aluminum titanate based composite porous ceramics with both high porosity and mechanical strength prepared by a special two-step sintering method
Yirong Wang,Xueqian Wang,Chuanbao Liu,Xiaopo Su,Chengye Yu,Yanjing Su,Lijie Qiao,Yang Bai
DOI: https://doi.org/10.1016/j.jallcom.2020.157193
IF: 6.2
2021-02-01
Journal of Alloys and Compounds
Abstract:<p>In this work, we develop a two-step sintering technology special for porous ceramics to resolve the contradiction between porosity and mechanical strength. It contains a first long-time sintering at the relatively low temperature (T<sub>1</sub>) and a second fast sintering at higher temperature (T<sub>2</sub>). Porous ceramics of aluminum titanate-strontium feldspar-mullite (ASM) ternary composite were prepared by this method, and exhibit both high porosity and high mechanical strength. The effects of T<sub>1</sub> and T<sub>2</sub> on the phase composition, microstructure, porosity, pore size distribution, mechanical strength and thermal expansion coefficient (TEC) of ASM porous ceramics are systematically studied. The sample sintered at T<sub>1</sub> = 1400 °C & T<sub>2</sub> = 1500 °C shows optimum performance: the porosity, bulk density, and mean pore diameter (D<sub>50</sub>) are 63.48%, 1.20 g/cm<sup>3</sup> and 15.94 μm, respectively; while the flexural strength reaches 9.22 MPa and the TEC is 2.9 × 10<sup>−6</sup>/K. The two-step sintering technology provides a powerful tool to develop porous ceramics with excellent comprehensive properties.</p>
materials science, multidisciplinary,chemistry, physical,metallurgy & metallurgical engineering