The influence of different additives on microstructure and mechanical properties of aluminum titanate ceramics

Weiwei Chen,Anze Shui,Qingliang Shan,Jiawei Lian,Cong Wang,Jianqiao Li

DOI: https://doi.org/10.1016/j.ceramint.2020.08.234

IF: 5.532

2021-01-01

Ceramics International

Abstract:<p>The aluminum titanate (AT: Al₂TiO₅) ceramics with different additives, including SiO₂, MgO, Fe₂O₃ and their mixture, were prepared by reaction sintering at 1500 °C in air for 2 h. The influence of additives on the microstructure and flexibility of AT ceramics is studied. Research illustrates that additives, MgO, Fe₂O₃ and their mixture, can be dissolved in AT ceramics to promote the formation of elongated grains and grain boundary microcracks. The elongated grains can interlock together and restrain crack propagation while microcracks can provide gaps for grains to move, leading to obvious flexibility of sample. Especially, the AT ceramics doped with MgO and Fe₂O₃ (ATFM) show the optimum flexibility with a deflection about 0.55 mm and strength up to 13.85 MPa. While the additive of SiO₂ can reduce the size of grains and microcracks, resulting in high mechanical strength but poor flexibility. The successful fabrication of such AT flexible ceramics will provide potential opportunity for anti-vibration and refractory application.</p>

materials science, ceramics