Effects of Composite Systems on Sintering Properties of Aluminum Oxide Ceramics
Liang Li
DOI: https://doi.org/10.1080/10584587.2021.1911251
2021-06-13
Integrated Ferroelectrics
Abstract:Because aluminum oxide ceramics have excellent properties, such as high strength, high hardness, good resistance to chemical corrosion, and chemical stability, aluminum oxide ceramics have been used widely in the fields of machinery, chemical industry, environment protection, electronic engineering, metallurgy, and composite materials. During the preparation of aluminum oxide ceramics, an appropriate composite system is important because it is effective for decreasing the sintering temperature and improving the properties of aluminum oxide ceramics. In the present work, powders of alumina, calcium oxide, zirconium dioxide, titanium dioxide, and silica sand were used as the main raw materials to design different composite systems, and then aluminum oxide ceramics were prepared via a semi-dry pressing method. Effects of different composite systems on the sintering property of aluminum oxide ceramics were studied. The results indicate that the CaO–SiO2–TiO2 system effectively improves the composition and structure of the aluminum oxide ceramic and significantly enhances the flexural strength of the aluminum oxide ceramic; the optimal formulation of adding CaO, SiO2, and TiO2 in the CaO–SiO2–TiO2 composite system is 4%, 2%, and 3%, respectively, and this formulation leads to a maximum flexural strength of 146.48 MPa; adding an appropriate amount of TiO2 can promote the formation of a corundum phase and refined grains and therefore enhances the fracture toughness of aluminum oxide ceramics.
engineering, electrical & electronic,physics, condensed matter, applied