Microstructure and mechanical properties of CaAl12O19 reinforced Al2O3-Cr2O3 composites
Kunkun Cui,Tao Fu,Yingyi Zhang,Jie Wang,Haobo Mao,Tianbiao Tan
DOI: https://doi.org/10.1016/j.jeurceramsoc.2021.08.024
IF: 5.7
2021-12-01
Journal of the European Ceramic Society
Abstract:Al2O3-Cr2O3 refractories have excellent slag corrosion resistance and can adapt to the oxidation/reduction atmosphere in the smelting reduction ironmaking furnace. However, Al2O3-Cr2O3 refractories have poor mechanical properties and sintering properties. In order to improve the mechanical properties of Al2O3-Cr2O3 materials, the CaAl12O19 reinforced Al2O3-Cr2O3 composites were prepared by pressureless sintering process, and the influences of CaO content on the sintering properties, mechanical properties, and microstructure evolution of the composites were studied. The results show that a small amount of CaO can significantly improve the compactness of the composites, which is mainly due to the formed sheet-like CA6 fill the gap between the solid solutions, and reduces the porosity of the composites. In addition, the sheet-like CA6 makes the connection between solid solutions closer, and the intergranular fracture gradually transforms into a mixed mode of intergranular and transgranular fracture. The best mechanical propertie is observed at S4 with the CaO content of 2 wt.%. Compared with sample S0 without CaO, the hardness, compressive strength and flexural strength of the S4 were increased by 35.19 %, 49.69 %, and 68.34 %, respectively. The addition of excessive CaO will deteriorate the mechanical properties of the composites, because the formation of a large number of layered CA6 increases the porosity of the composites. Furthermore, a small amount of CaO addition can significantly improve the thermal shock resistance of the composites. After 10 and 20 thermal shock cycles, the strength loss rates of S4 are only 5.83 % and 8.74 %, respectively.
materials science, ceramics