Sintering, densification and crystallization of Ca–Al–B–Si–O glass/Al 2 O 3 composites for LTCC application

Ming Liu,Hongqing Zhou,Xiaoying Xu,Zhenxing Yue,Min Liu,Haikui Zhu

DOI: https://doi.org/10.1007/s10854-013-1351-7

2013-01-01

Abstract:Ca–Al–B–Si–O glass/Al 2 O 3 composites were prepared based on the borosilicate glass powders (D 50 = 2.84) and Al 2 O 3 ceramic powders (D 50 = 3.26), and the sintering, densification, crystallization of samples were investigated. The shrinkage of sample starts to have a sharp increase at 600 °C. The shrinkage of sample starts to have a further rapid increase after the glass softening temperature of about 713 °C. Glass/Al 2 O 3 composites can be sintered at 875 °C/15 min and exhibit better properties of a relative density of 98.4 %, a λ value of 2.89 W/mK, a ε r value of 7.82 and a tan δ value of 5.3 × 10 −4 . The interface between glass and Al 2 O 3 grains and the interface between anorthite and glass phase depicts a good compatibility according to transmission electron microcopy test. It is the low sintering temperature, high density and good compatibility with Ag electrodes that, guarantee borosilicate glass/Al 2 O 3 composites suitable for low temperature co-fired ceramic materials.