Abstract:The effects of alkaline-earth oxides (SrO, CaO, MgO) on the densification and microwave properties of low-temperature fired BaO–Al2O3–SiO2 (BAS) glass–ceramic/Al2O3 composites have been investigated. By adding alkaline-earth oxides, the softening and crystallization behaviors of BAS-based glass–ceramics, which determine the densification of composites, are sequentially weakened in the order of BAS, SrO–BaO–Al2O3–SiO2 (SBAS), CaO–BaO–Al2O3–SiO2 (CBAS) and MgO–BaO–Al2O3–SiO2 (MBAS). It is also found in the above BAS-based glass–ceramics that the addition of alkaline-earth oxides plays a more profound role on crystallization behavior than on softening behavior, leading to the expansion of the interval between crystallization and softening temperatures (i.e., densification temperature range) to different degrees depending on the type of oxides added. As a result, the microstructures of oxides-modified glass–ceramic/Al2O3 composites (SBAS/Al2O3, CBAS/Al2O3, MBAS/Al2O3) are much denser than those of BAS/Al2O3. The properties of such composites are determined by the interplay among density of microstructure, amount and relative ratio of crystalline and residual glass phases related to the crystallization behavior and interfacial reaction. Detailed analyses suggest that CBAS/Al2O3 achieves optimal properties among all the four composites. Specifically, for CBAS/Al2O3 the dielectric constant, dielectric loss, bending strength and CTE value are 5.81 ± 0.12 (at ~ 10 GHz), (2.04 ± 0.12) × 10−3 (at ~ 10 GHz), 155 ± 7 MPa and 6.58 ± 0.11 ppm/°C, respectively. Our findings may provide a new avenue to design LTCC substrate materials as feasible candidates for microwave devices.

Microstructure and Dielectric Properties of Ca-Al-B-Si-O Glass/Al2o3 Composites with Various Alkali Oxides Contents

Low Temperature Sintering and Dielectric Properties of Ca- Ba-Al-B-Si-O Glass/Al_2 O_3 Composites for LTCC Applications

Microstructure and dielectric properties of glass/Al 2 O 3 composites with various low softening point borosilicate glasses

Sintering Characteristics, Microstructures and Dielectric Properties of Borosilicate-Based Glass/alpha-Al2o3 Composites for LTCC Application with Different MgO and Na2O Contents

Effect of Different Forms of Silica on Sintering, Microstructure and Properties of Borosilicate Glass/al2o3 Composites

Effects of Various Fillers on Sintering, Microstructures and Properties of Ca-Ba-Al-B-Si-O Glass/ceramic Composites

Study on properties of CaO-B 2O 3-SiO 2 glass ceramics contained alkali ions

Sintering, densification and crystallization of Ca–Al–B–Si–O glass/Al 2 O 3 composites for LTCC application

The size-effect of Al2O3 on the sinterability, microstructure and properties of glass-alumina composites

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Low Temperature Sintering and Properties of Ca–Al–B–Si–O Glass/ceramic Composites with Various Ceramic Fillers

Effect of Al2O3 on the Dielectric Properties and Microstructures of CaO-B2O3-SiO2 System Glass Ceramics

Effects of Alkaline Earth Oxides on the Densification and Microwave Properties of Low-Temperature Fired BaO–Al2O3–SiO2 Glass–ceramic/al2o3 Composites

Effect of silica addition on microstructure, sintering behavior, and dielectric properties of borosilicate glass/alumina composites for LTCC application

Effect of CaO Content on Structure and Properties of Low Temperature Co-Fired Glass–ceramic in the Li2O–Al2O3–SiO2 System

Microstructure, Thermal, Mechanical, and Dielectric Properties of BaO–CaO–Al2O3–B2O3–SiO2 Glass-Ceramics

Microstructure, Thermal, Mechanical, and Dielectric Properties of BaO-CaO-Al2O3-B2O3-SiO2 Glass-Ceramics

Crystallization, sinterability and dielectric properties of CaO–B 2 O 3 –SiO 2 glass ceramics with Al 2 O 3 additives

Microstructure and microwave dielectric properties of CaO-B2O3-SiO2 glass ceramics with various B2O3 contents

Low temperature sintering and characteristics of K2O–B2O3–SiO2–Al2O3 glass/ceramic composites for LTCC applications

Effect of SiO2 content on the sintering kinetics, microstructures and properties of BaO-Al2O3-B2O3-SiO2 glass-ceramics for LTCC application