Abstract:SrO–BaO–B2O3–SiO2 glass-ceramics with a high dielectric constant and low dielectric loss were prepared. The influence of the SiO2/BaO ratio on the sintering behavior, crystallization behavior, and properties were systematically investigated. The results showed that the increasing amount of liquid phase from increasing the SiO2/BaO ratio promoted sintering, resulting in an initial decrease in the sintering activation energy. However, the viscosity of the liquid phase continued to increase, leading to an increase in the sintering temperature and sintering activation energy when the SiO2/BaO ratio reached 0.90. As the SiO2/BaO ratio increased, the fraction of the primary phase BaSi2Al2O8 increased, and its grains grew; the minor phase SrTiO3 was suppressed, resulting in changes in the properties of the glass-ceramics. The sample with a SiO2/BaO ratio of 0.69, which was sintered at 850 °C for 10 min, showed excellent properties: a coefficient of thermal expansion (CTE) of 10.63 × 10−6 K−1 (25–500 °C), a dielectric constant (ϵr) of 16.24 (1 MHz), a dielectric loss (tanδ) of 3.39 × 10−3 (1 MHz), a flexural strength of 138.80 MPa, and a quality loss of acid corrosion of 1.06 × 10−4 g mm−2. The results indicated that the SrO–BaO–B2O3–SiO2 glass-ceramics used in this study have great potential for low-temperature co-fired ceramics applications.

Sintering and Properties of CaO-Al<sub>2</sub>O<sub>3</sub>-B<sub>2</sub>O<sub>3</sub>-SiO<sub>2</sub> System Glass Ceramics

Sintering and properties of CaO-Al2O3-B2O3-SiO2 system glass ceramics

Densification and Dielectric Properties of CaO–B2O3–SiO2 System Glass Ceramics

Influence of CaO content by mass in sintering aid and sintering temperature on the properties of Al2O3-based microwave ceramic materials

Low dielectric and high frequency glass-ceramic in the system CaO-B2O3-SiO2

Study of the Properties of CaF_2-AlF_3-SiO_2 Oxyfluoride Glass-Ceramic System

Effect of Al2O3 on the Dielectric Properties and Microstructures of CaO-B2O3-SiO2 System Glass Ceramics

Sintering,crystallization and Dielectric Properties of CaO-B 2 O 3 -Sio 2 System Glass Ceramics

Effect of SiO2/BaO ratio on sintering behavior, crystallization behavior, and properties of SrO–BaO–B2O3–SiO2 glass-ceramics

Characterizations of CaO–B2O3–SiO2 glass–ceramics: Thermal and electrical properties

Crystallization Behavior and Performance of MgO-Al2O3-SiO2 Glass-Ceramics by Sintering

Sintering Behavior, Microstructure and Mechanical Properties of Various Fluorine-Containing Y-SiAlON Glass-Ceramics

Effect of Ca/Si ratio on the microstructures and properties of CaO–B2O3–SiO2 glass-ceramics

Microstructure and Dielectric Properties of Ca-Al-B-Si-O Glass/Al2o3 Composites with Various Alkali Oxides Contents

Structure and sintering behavior of BaO–SrO–B2O3–SiO2 sealing glass for Al2O3 ceramic substrates

Low Temperature Sintering and Dielectric Properties of Ca- Ba-Al-B-Si-O Glass/Al_2 O_3 Composites for LTCC Applications

Crystallization, sinterability and dielectric properties of CaO–B 2 O 3 –SiO 2 glass ceramics with Al 2 O 3 additives

Low Temperature Sintering and Properties of Ca–Al–B–Si–O Glass/ceramic Composites with Various Ceramic Fillers

Effect of SiO2/Al2O3 ratio on sintering behavior, crystallization behavior and properties of diopside-anorthite glass-ceramics

Sintering Characteristics, Microstructures and Dielectric Properties of Borosilicate-Based Glass/alpha-Al2o3 Composites for LTCC Application with Different MgO and Na2O Contents

Sintering and Properties of CaO-Al&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;3&lt;/sub&gt;-B&lt;sub&gt;2&lt;/sub&gt;O&lt;sub&gt;3&lt;/sub&gt;-SiO&lt;sub&gt;2&lt;/sub&gt; System Glass Ceramics