Low Temperature Sintering and Properties of Ca–Al–B–Si–O Glass/ceramic Composites with Various Ceramic Fillers
Ming Liu,Hongqing Zhou,Min Liu,Zhenxing Yue,Haikui Zhu
DOI: https://doi.org/10.1007/s10854-013-1075-8
2013-01-01
Journal of Materials Science Materials in Electronics
Abstract:Low-temperature sintering and properties of low temperature co-fired ceramics materials based on a typical Ca–Al–B–Si–O glass and various ceramic fillers such as (Zr0.8Sn0.2)TiO4, (Ca0.5Mg0.5)TiO3, BaSm2Ti4O12 and CaTiO3 were investigated. Densification, crystallization and dielectric properties are found to strongly depend on the type of filler. The densification process of glass/ceramic composites with different ceramic fillers is mainly from 600 to 925 °C, and the initial compacting temperature of samples is 600 °C. The initial rapid densification of samples starts after glass softening temperature of samples. The XRD patterns of (Ca0.5Mg0.5)TiO3 and CaTiO3 samples demonstrate crystalline phases, CaTiO(SiO4) and CaTiSiO5, respectively, as a result of firing at 875 °C for 15 min. The high dielectric constant fillers produce high εr values of the dielectric samples. The maximum dielectric constant of samples for (Zr0.8Sn0.2)TiO4, (Ca0.5Mg0.5)TiO3, BaSm2Ti4O12 and CaTiO3 filler is 14.02, 16.21, 18.64 and 23.78, respectively. Comparing with other samples, the specimens for (Ca0.5Mg0.5)TiO3 and CaTiO3 ceramic filler have lower dielectric loss. Especially, the sample for (Ca0.5Mg0.5)TiO3 filler exhibits the lowest dielectric loss of 0.00011.