Abstract:Solutions containing hydroxy-SiAl(HSA) oligocations were prepared by two procedures: (1) treatment of a mixture of silicic acid, which was prepared by dispersing silica sol in an ultrasonic generator, and AlCl3 with aqueous NaOH, followed by aging of the product and (2) preliminary preparation and aging of hydroxy-Al13 oligocations followed by reaction of the latter with silicic acid. Exchange of Na-montmorillonite with HSA oligocations yielded pillared clays (designated as SiAl-PILC obtained using method 1, and GSiAl-PILC obtained using method 2) showing mixed maximum d(001) values of 2.65 and 1.90 nm for air-dried samples and maximum surface areas of approximately 267 m2/g after outgassing at 200-degrees-C/101 kPa. Elemental analysis showed a gradual increase in the Si/Al ratio in the intercalated HSA oligocations with increasing Si/Al ratio in the pillaring solution. The pillaring structure, thermal stability, and surface acidity of the pillared clay products have been determined using Al-27-NMR, X-ray diffraction (XRD), XPS, DTA, IR, and temperature-programmed desorption (TPD) measurements. The results suggest that the thermal stability of the pillared clays was improved by incorporating silica. Hydroxy-SiAl pillared clays show sharply higher concentrations of strong acid sites, especially Bronsted acid sites, compared with reference Al-PILC obtained by pillaring with hydroxy-Al13 oligocations. This increased acidity is probably due to the presence of acidic, surface silanol groups in the HSA oligocations. The cracking of cumene and the disproportionation and alkylation of 1,2,4-trimethylbenzene were carried out in a pulse reaction system at 400-degrees-C over the pillared clay catalysts. Incorporating silica into an alumina pillar increased the cracking activity of cumene and the activity and selectivity for the disproportionation of 1,2,4-trimethylbenzene compared to those observed for Al-PILC.

Preparation and characterization of silica-pillared layered titanate

Preparation and characterization of a silica-pillared layered lanthanum titanate

Preparation of Layered Ferrititanate Pillared by Silica

Syntheses and Characterization of Silica - Pillared Layered Ferrititanates

Preparation of Silica-Pillared Layered Tetratitanate with a High Surface Area

Highly Thermostable, Porous, Layered Titanoniobate Pillared by Silica

Reaction of tetrabutyl titanate in the adsorption layer on Si02 surface

Preparation and Characterization of Alumina-Pillared Layered Titanate with A High Interlayer Spacing

Synthesis and characterization of titania-pillared layered HLaNb2O7 with high specific surface area

Preparation and Characterization of Tio2-Pillared Layered Hnb3o8

Synthesis Of Titania-Pillared Layered Niobic Acid With A High Specific Surface Area By Using Sol-Intercalation Method

Synthesis and Characterization of Alumina-Pillared Layered Tetratitanates with Different Interlayer Spacings

SYNTHESIS OF AL2O3-PILLARED LAYERED TITANONIOBATE

Preparation of Alumina-pillared Layered Titanoniobates with Different Interlayer Distances

Atomic layer deposition of TiO2 on mesoporous silica

Silica–Titania mixed Oxides: Si–O–Ti Connectivity, Coordination of Titanium, and Surface Acidic Properties

Synthesis and Characterization of Porous Chromia-Pillared Layered Titanoniobate

Epoxidation of Propylene with Dilute H 2 O 2 over Titanium Silicalite Containing Trace Aluminum

Synthesis of easily shaped ordered mesoporous titanium-containing silica

Preparation and Characterization of Hierarchically Porous Monolithic TiO2

Preparation and Characterization of Hydroxysilicoaluminum Pillared Clays