Abstract:TiO2-diatomite photocatalysts were prepared by sol-gel process with various pre-modified diatomite. In order to obtain diatomite with different surface characteristics, two modification approaches including calcination and phosphoric acid treatment on the micro-structure of diatomite are introduced. The photocatalysts were characterized by XRD, XPS, nitrogen adsorption-desorption isotherms and micromorphology analysis. The results indicate that, compared with pure TiO2, the anatase-to-rutile phase transition temperature of TiO2 loaded on diatomite carrier is significantly increased to nearly 900 degrees C, depending on the different pretreatment method of diatomite. The photocatalytic activities of different samples were evaluated by their degradation rate of methyl orange ( MO) dye under UV and visible-light irradiation. The samples prepared by phosphoric acid pretreatment method exhibit the highest photocatalytic activity. After 90 min of UV irradiation, about 90% of MO is decomposed by the best effective photocatalyst. And after 8 h visible-light irradiation, nearly 60% of MO is decomposed by the same sample. Further mechanism investigation reveals that the H3PO4 pretreatment process can obviously change the surface features of diatomite carrier, cause the formation of Si-O-Ti bond, increase the binding strength between TiO2 and diatomite, restrain crystal growth of loaded TiO2, and thus form thermal-stable meso-porous structure at the granular spaces. It helps to build micro-, meso- and macro-porous hierarchical porous structure in TiO2-diatomite, and improves the charge and mass transfer efficiency during catalyzing process, resulting in the significantly increased photocatalytic activity of TiO2-diatomite pretreated by phosphoric acid. (C) 2014 Elsevier B. V. All rights reserved.

Reaction of tetrabutyl titanate in the adsorption layer on Si02 surface

INFLUENCE OF WATER CONTENT ON CONTENT AND CHARACTERISTIC OF TiO2 DURING PREPARATION OF TiO2 NANOPARTICLES ON SiO2 SURFACE

Study on Adsorption and Reaction Mechanism of Preparation of TiO2/SiO2 by Adsorption Phase Reactor Technique

PREPARATION OF NANO TiO2 ON SURFACE OF SILICA

Reaction Mechanism of Preparation of Nano TiO2 by Adsorption Phase Reaction Technique

Preparation of TiO2 nanoparticles on the surface of SiO2 in binary liquids

Preparation of Tio2 Nanoparticles on Surface of Different Supports by Adsorption Phase Reaction Technique

Influence of temperature on preparation of TiO2 nanoparticles by adsorption phase nanoreactor technique

Preparation of Nanometer Tio2/Sio2 Composite Materials by Adsorption Phase Nanoreactor Technique

Preparation of Tio2 Nanoparticles on Different Sio2 Supports by the Adsorption Phase Technique

Influence Of Crystallization Of Nano Tio2 Prepared By Adsorption Phase Synthesis On Photodegradation Of Gaseous Toluene

Preparation of TiO_2/SiO_2 and Photo-Catalytic Degradation of Methyl-Orange

Adsorption Geometry of Tetracene on SiO2/Si (111) Substrate with the Balance of Molecule–substrate and Intermolecular Interaction

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Atomic layer deposition of TiO2 on mesoporous silica

IR-analysis of H-bonded H2O on the pure TiO2 surface

The Adsorption and Reaction of a Titanate Coupling Reagent on the Surfaces of Different Nanoparticles in Supercritical CO2.

Specific and High-Affinity Adsorption of Volatile Organic Compounds on Titanium Dioxide Surface

Surface Acidity and Properties of TiO2/SiO2 Catalysts Prepared by Atomic Layer Deposition: UV−visible Diffuse Reflectance, DRIFTS, and Visible Raman Spectroscopy Studies

Adsorption-Controlled Wettability and Self-Cleaning of TiO 2

Theoretical Study of the Molecular and Electronic Structure of Methanol on a TiO2(110) Surface