Abstract:In this article, we report a controllable and reproducible approach to prepare highly ordered 2-D hexagonal mesoporous crystalline TiO2-SiO2 nanocomposites with variable Ti/Si ratios (0 to infinity). XRD, TEM, and N2 sorption techniques have been used to systematically investigate the pore wall structure, and thermal stability functioned with the synthetic conditions. The resultant materials are ultra highly stable (over 900 degrees C), have large uniform pore diameters (approximately 6.8 nm), and have high Brunauer-Emmett-Teller specific surface areas (approximately 290 m2/g). These mesostructured TiO2-SiO2 composites were obtained using titanium isopropoxide (TIPO) and tetraethyl orthosilicate (TEOS) as precursors and triblock copolymer P123 as a template based on the solvent evaporation-induced co-self-assembly process under a large amount of HCl. Our strategy was the synchronous assembly of titanate and silicate oligomers with triblock copolymer P123 by finely tuning the relative humidity of the surrounding atmosphere and evaporation temperature according to the Ti/Si ratio. We added a large amount of acidity to lower condensation and polymerization rates of TIPO and accelerate the rates for TEOS molecules. TEM and XRD measurements clearly show that the titania is made of highly crystalline anatase nanoparticles, which are uniformly embedded in the pore walls to form the "bricked-mortar" frameworks. The amorphous silica acts as a glue linking the TiO2 nanocrystals and improves the thermal stability. As the silica contents increase, the thermal stability of the resulting mesoporous TiO2-SiO2 nanocomposites increases and the size of anatase nanocrystals decreases. Our results show that the unique composite frameworks make the mesostructures overwhelmingly stable; even with high Ti/Si ratios (> or =80/20) the stability of the composites is higher than 900 degrees C. The mesoporous TiO2-SiO2 nanocomposites exhibit excellent photocatalytic activities (which are higher than that for commercial catalyst P25) for the degradation of rhodamine B in aqueous suspension. The excellent photocatalytic activities are ascribed to the bifunctional effect of highly crystallized anatase nanoparticles and high porosity.

Silica–Titania mixed Oxides: Si–O–Ti Connectivity, Coordination of Titanium, and Surface Acidic Properties

PREPARATION OF NANO TiO2 ON SURFACE OF SILICA

Epoxidation of Propylene with Dilute H 2 O 2 over Titanium Silicalite Containing Trace Aluminum

Preparation and Characterization of Silica-modified Titanium Dioxide Nanoparticles by Co-precipitation Method

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Synthesis of Ti-containing mesoporous silicates from inorganic titanium sources

The synthesis and characterization of titanium silicalite-1

Characterization of titania silicalites

Preparation of TiO2/SiO2 Composite by Chemical Coating Method

Enhanced photocatalytic activity of titania–silica mixed oxide prepared via basic hydrolyzation

Effect of Embedded-Silica on Microstructure and Photocatalytic Activity of Titania Prepared by Ultrasound-Assisted Hydrolysis

Direct Synthesis and Structural Characteristics of Titanium Dioxide/Mesoporous SBA-15 Materials

Incorporation of Titanium into Mesoporous Silica Molecular Sieve SBA-15

Control of Ti Active-Site Microenvironment in Titanosilicate Catalysts and Its Effect on Oxidation Pathways

Sol–gel derived organic–inorganic hybrid from trialkoxysilane-capped acrylic resin and titania: effects of preparation conditions on the structure and properties

Synthesis of titanium silicalite-1 (TS-1) zeolite with high content of Ti by a dry gel conversion method using amorphous TiO2–SiO2 composite with highly dispersed Ti species

Controllable and Repeatable Synthesis of Thermally Stable Anatase Nanocrystal-Silica Composites with Highly Ordered Hexagonal Mesostructures.

Synthesis of Ti-Containing Silica Mesoporous Molecular Sieves with High Catalytic Activity for Epoxidation

Stabilisation of molecular TiO4 species on the pore surface of mesoporous silica for photocatalytic H2 evolution

Synthesis and characterization of titanium silicate molecular sieves with zorite-type structure

Synthesis of Mesoporous Tetragonal ZrO2, TiO2 and Solid Solutions and Effect of Colloidal Silica on Porosity