Abstract:This paper investigates the effect of the variation in alkoxide precursor ratio and templating agent concentration on the production of titanium silicalite (TS-1) through analysis using various physical characterisation techniques. X-ray diffraction showed clear evidence for the MFI zeolite structure and a high degree of crystallinity in all systems. For those materials prepared using a templating agent with ultra low alkali metal content, excellent agreement with previously reported unit cell parameters was obtained. For these same systems, 20% higher specific surface areas were also obtained by nitrogen adsorption. Analysis using an energy dispersive x-ray spectrometer coupled to a scanning electron microscope showed that the product typically contained between 60 and 90% of the titanium in the precursor and some dependence of titanium incorporation on the initial mixture composition was also observed. The results from Raman spectroscopy indicated titanium incorporation into the silicalite framework for all systems. For those materials produced using a templating agent with low alkali metal content, extra-framework anatase titanium dioxide was also identified at moderate Ti : Si mole ratios (>0.03) in the initial mixture. Due to its lower penetration depth, x-ray photoelectron spectroscopy (XPS) was used to characterise the titanium species in the surface layer. The XPS results indicated that a small amount of extra-framework titania was present in the surface of most of the TS-1 samples and the proportion of extra-framework material was observed to increase with both precursor alkali metal content and precursor titanium to silicon ratio.

Incorporation of Titanium into Mesoporous Silica Molecular Sieve SBA-15

Synthesis of Ti-containing mesoporous silicates from inorganic titanium sources

Direct Synthesis of Titanium Substituted SBA-15 under Conventional Hydrothermal Conditions and Their Catalysis Characterization

Direct Synthesis, Characterization and Catalytic Activity of Titanium-Substituted Sba-15 Mesoporous Molecular Sieves

Direct Synthesis and Structural Characteristics of Titanium Dioxide/Mesoporous SBA-15 Materials

Synthesis and characterization of Ti-SBA-16 ordered mesoporous silica composite

Ti incorporation in MCM-41 mesoporous molecular sieves using hydrothermal synthesis

Synthesis, Characterization and Catalytic Performance of Ti-Containing Mesoporous Molecular Sieves Assembled from Titanosilicate Precursors

Synthesis of easily shaped ordered mesoporous titanium-containing silica

The modification of titanium in mesoporous silica for Co-based Fischer-Tropsch catalysts

The synthesis and characterization of titanium silicalite-1

Atomic layer deposition of TiO2 on mesoporous silica

Incorporation of titanium into polymorph C of zeolite beta

Characterization of Ti/SBA-15 Composites Synthesized by Chemical Vapour Deposition of Organic Titanium Compounds

Preparation and Characterization of Titanium-Containing MFI from Highly Siliceous ZSM-5: Effect of Precursors Synthesized with Different Templates

Stabilisation of molecular TiO4 species on the pore surface of mesoporous silica for photocatalytic H2 evolution

Synthesis and characterization of titanium silicate molecular sieves with zorite-type structure

Ordered Mesoporous Titanosilicates with Better Catalytically Active Titanium Sites Assembled from Preformed Titanosilicate Precursors with Zeolite Building Units in Alkaline Media

Post-Grafting Preparation Of Large-Pore Mesoporous Materials With Localized High Content Titanium Doping

Synthesis, characterization and application of MTS-9 with different content of titanium

Synthesis, characterization and catalytic properties of low cost titanium silicalite