Abstract:Novel mesostructured fitanosilicates designated as MTS-9 have been successfully synthesized from assembly of preformed nanosized titanosilicate precursors with polymer surfactants. Mesoporous MTS-9 shows highly hydrothermal stability in boiling water (over 120 h) as compared with that of Ti-MCM-41 and SBA-15. In phenol hydroxylation, Ti-MCM-41 shows very low catalytic activity (2.5%), but MTS-9 exhibits very high catalytic activity, with phenol conversion of 26%, which is comparable with TS-1. In styrene epoxidation, MTS-9 shows high activity and selectivity similar to those of TS-1, which are much different from those of Ti-MCM-41. In 2,3,6-trimethylphenol hydroxylation, Ti-MCM-41 is inactive because of the relatively low oxidation ability of Ti species in the amorphous wall of Ti-MCM-41, and TS-1 is also inactive because of the inaccessibility of the small micropores of TS-1 to the large diameter of a bulky molecule like 2,3,6-trimethylphenol. However, MTS-9 is very active for this reaction with conversion of 18.8% indicating that MTS-9 is an effective catalyst for the oxidation of bulky molecules. The MTS-9 samples were characterized with infrared, UV-visible, UV-Raman, and numerous other techniques. The results suggest that the titanium species in MTS-9 are TS-1-like, and that the pore walls of MTS-9 contains primary and secondary structural building units, similar to those of microporous zeolites. Such unique structural features might be responsible for the observed strong oxidation ability and high hydrothermal stability of the mesostructured titanosilicates. Heating MTS-9 at 500 degreesC leads to the transformation of titanium species, giving relatively low catalytic conversion in phenol hydroxylation, which suggests that increasing thermal stability of titanium sites like TS-1 species in the mesoporous wall is still a great task for preparation of mesostructured titanosilicates.

Characterization of titania silicalites

Silicene-supported TiO2 Nanostructures: a Theoretical Study of Electronic and Optical Properties

Visible-Light-Driven Titania/Silica Photocatalyst Co-Doped with Boron and Ferrum

The synthesis and characterization of titanium silicalite-1

Silica–Titania mixed Oxides: Si–O–Ti Connectivity, Coordination of Titanium, and Surface Acidic Properties

Titanium species in titanium silicalite TS-1 prepared by hydrothermal method

Synthesis, Characterization and Catalytic Performance of Ti-Containing Mesoporous Molecular Sieves Assembled from Titanosilicate Precursors

Effect of Embedded-Silica on Microstructure and Photocatalytic Activity of Titania Prepared by Ultrasound-Assisted Hydrolysis

A KIND OF INACTIVE TITANIUM SPECIES IN TITANIUM SILICALITE

Nature of Reactive Sites in TS-1 from 15N solid-state NMR and Ti K-edge X-Ray Absorption Spectroscopic Signatures upon Pyridine Adsorption

Epoxidation of Propylene with Dilute H 2 O 2 over Titanium Silicalite Containing Trace Aluminum

Surface Acidity and Properties of TiO2/SiO2 Catalysts Prepared by Atomic Layer Deposition: UV−visible Diffuse Reflectance, DRIFTS, and Visible Raman Spectroscopy Studies

Ordered Mesoporous Titanosilicates with Better Catalytically Active Titanium Sites Assembled from Preformed Titanosilicate Precursors with Zeolite Building Units in Alkaline Media

Synthesis, characterization and catalytic performance of titanium silicalite-1 prepared in micellar media

Interface Actions Between TiO2 and Porous Diatomite on the Structure and Photocatalytic Activity of TiO2-diatomite

Incorporation of Titanium into Mesoporous Silica Molecular Sieve SBA-15

Synthesis, Characterization, and Catalytic Activity of Mesostructured Titanosilicates Assembled from Polymer Surfactants with Preformed Titanosilicate Precursors in Strongly Acidic Media

GROWING OF NANOSTRUCTURED TITANIUM-SILICALITE ON AMORPHOUS TITANIA AND ITS CATALYTIC ACTIVITY IN EPOXIDATION

Preparation and Characterization of Titania Ion-Sieves

Synthesis and characterization of titanium silicalite TS-1 prepared using phosphonium ions

Synthesis, characterization and catalytic properties of low cost titanium silicalite