Abstract:This paper investigates the effect of the variation in alkoxide precursor ratio and templating agent concentration on the production of titanium silicalite (TS-1) through analysis using various physical characterisation techniques. X-ray diffraction showed clear evidence for the MFI zeolite structure and a high degree of crystallinity in all systems. For those materials prepared using a templating agent with ultra low alkali metal content, excellent agreement with previously reported unit cell parameters was obtained. For these same systems, 20% higher specific surface areas were also obtained by nitrogen adsorption. Analysis using an energy dispersive x-ray spectrometer coupled to a scanning electron microscope showed that the product typically contained between 60 and 90% of the titanium in the precursor and some dependence of titanium incorporation on the initial mixture composition was also observed. The results from Raman spectroscopy indicated titanium incorporation into the silicalite framework for all systems. For those materials produced using a templating agent with low alkali metal content, extra-framework anatase titanium dioxide was also identified at moderate Ti : Si mole ratios (>0.03) in the initial mixture. Due to its lower penetration depth, x-ray photoelectron spectroscopy (XPS) was used to characterise the titanium species in the surface layer. The XPS results indicated that a small amount of extra-framework titania was present in the surface of most of the TS-1 samples and the proportion of extra-framework material was observed to increase with both precursor alkali metal content and precursor titanium to silicon ratio.

Synthesis, characterization and catalytic performance of titanium silicalite-1 prepared in micellar media

Synthesis, characterization and catalytic performance of titanium silicalite-1 prepared in the presence of nonionic surfactants

Synthesis of Titanium Silicalite-1 with Small Crystal Size by Using Mother Liquid of Titanium Silicalite-1 As Seed

Synthesis of TS-1 Using Amorphous SiO2 and Its Catalytic Properties for Hydroxylation of Phenol in Fixed-Bed Reactor

Characterization and catalytic properties of TS-1 synthesized with mixed templating reagent instead of TPAOH

Low-Cost Synthesis of Titanium Silicalite-1 (TS-1) with Highly Catalytic Oxidation Performance through a Controlled Hydrolysis Process

Epoxidation of Propylene with Dilute H 2 O 2 over Titanium Silicalite Containing Trace Aluminum

The synthesis and characterization of titanium silicalite-1

Synthesis of titanium silicalite (TS-1) from the TPABr system and its catalytic properties for epoxidation of propylene

Synthesis of titanium silicalite-1 (TS-1) zeolite with high content of Ti by a dry gel conversion method using amorphous TiO2–SiO2 composite with highly dispersed Ti species

Synthesis of High-Performanced Titanium Silicalite-1 Zeolite at Very Low Usage of Tetrapropyl Ammonium Hydroxide

Studies on the synthesis of titanium silicalite, TS-1

Crystallization of titanium silicalite-1 (TS-1) from gels containing hexanediamine and tetrapropylammonium bromide

Synthesis of titanium silicalite-1 using amorphous SiO2 as silicon source

Titanium silicalite-1 catalytic architecture: A new approach to make TS-1 applicable to industrial process

Study on the Synthesis of Clay-Based Titanium Silicalite-1 Catalytic Composite

Synthesis, characterization and catalytic properties of low cost titanium silicalite

Epoxidation of allyl alcohol to glycidol using titanium silicalite TS-1: effect of the method of preparation

Synthesis of TS-1 Molecular Sieves Using Mixed Silicon Sources and Their Catalytic Performance for Removing Thiophene

Synthesis of TS-1 macro-nanosheets with improved catalytic performance in alkene epoxidation