Abstract:Oligomeric chromium(III)-intercalated titanoniobate has been prepared by the intercalation of propylamine into KTiNbO5 followed by substitution of propylammonium for tetramethylammonium and finally refluxing with an aqueous solution of Cr(O(2)CMe)(3). The first chromia-pillared layered titanoniobate was then obtained by calcination of oligomeric chromium(III)-intercalated titanoniobate at 400 degrees C in a flow of N-2. Characterization of chromia-pillared titanoniobate revealed that the material has the porous layered structure with a Brunauer-Emmett-Teller surface area of 122.4 m(2) g(-1) and an interlayer distance of 13.4 Angstrom as well as a narrow pore-size distribution in the range 30-46 Angstrom. The layered structure can be retained up to 500 degrees C. However, calcination of the oligomeric chromium(III)-intercalated titanoniobate in air at the same temperature led to a product with a low Surface area and a small interlayer space. X-Ray photoelectron studies indicate the existence of different states of chromia in the products obtained in the different atmospheres. The IR spectra of the pyridine-adsorbed material and the ammonia temperature-programmed desorption profile demonstrate the presence of a large amount of acid sites with medium strength on the surface of the new chromia-pillared material. Isopropyl alcohol decomposition confirms the existence of only acid sites in the sample.

Preparation of Porous Chromia-Pillared Titanoniobate

Synthesis of Porous Chromia-Pillared Tetratitanate

Synthesis and Characterization of Porous Chromia-Pillared Layered Titanoniobate

Preparation of Porous Chromia-Pillared Molybdenum Trioxide

Synthesis and Characterization of Chromia-Pillared Layered Tetratitanate

Preparation and Characterization of Layered Molybdenum Trioxide Pillared with Chromia

Synthesis and Characterization of Porous Chromia-Pillared Layered Lanthanum Niobic Acid

The First Systhesis of a Chromia-Pillared Layered Niobate with Porosity, Acidity and High Thermostability

Highly Thermostable, Porous, Layered Titanoniobate Pillared by Silica

SYNTHESIS AND CHARACTERIZATION OF CHROMIA PILLARED LAYERED NIOBATE

Preparation and catalytic properties of chromia-pillared α-zirconium phosphate

Preparation of Silica-Pillared Layered Tetratitanate with a High Surface Area

Preparation And Characterization Of One-Dimensional Porous Zinc Oxide Constructed By Nanocrystal

Studies on preparation and selective oxidation activities of chromia-pillared zirconium phenylphosphonate

Preparation and Characterization of Tio2-Pillared Layered Hnb3o8

Preparation of Alumina-pillared Layered Titanoniobates with Different Interlayer Distances

Selective oxidation on chromia-pillared zirconium phosphate and phenylphosphonate

SYNTHESIS OF AL2O3-PILLARED LAYERED TITANONIOBATE

Preparation and characterization of a silica-pillared layered lanthanum titanate

Preparation Of Three-Dimensional Chromium Oxide Porous Single Crystals Templated By Sba-15

Preparation and characterization of silica-pillared layered titanate