Synthesis and Characterization of Chromia-Pillared Layered Tetratitanate
WH Hou,YS Chen,CX Guo,QJ Yan,Y Chen,J Chen
DOI: https://doi.org/10.1002/cjoc.19990170208
IF: 5.56
1999-01-01
Chinese Journal of Chemistry
Abstract:The first chromia-pillared layered tetratitanate was prepared by the reaction of layered tetramethy-lammonium tetratitanate with chromium（Ⅲ） acetate [Cr（OAc）3] aqueous solution and subsequent calcination of the resultant solid product in air at 400℃. The obtained chromia-pillared layered tetratitanate has an interlayer distance of 1.06 nm and a high thermal stabih’ty up to 600℃. It was also found that calcination in N2 led to the chromia-pillared layered tetratitanate with relatively higher Brunauer-Emmett-Teller （BET） specific surface area （93.9 m2·g-1） and smaller average pore diameter （4.44 nm） than that in air （82.0 m2·g-1, 7.61 nm） . Both Bronsted and Lewis acid sites （mainly Lewis type） are present on the chromia-pillared layered tetratitanate （500℃, N2, 8 h） and strong enough to still remain a small proportion of pyridine upon outgassing at 250℃. Moreover, ammonia temperature-programmmed desorption （NH3-TPD） result showed that there were three NH3 desorption peaks at 160, 200and315℃, resp