Abstract:This study aims to investigate the influence of Cr content on the high-temperature mechanical, oxidation, and electrical properties of powder metallurgy ferritic stainless steel for solid oxide fuel cell (SOFC) interconnect. To achieve this objective, ferritic stainless steel water-atomized powders with different Cr content were first compacted and then sintered at 1380 °C for 2 h under hydrogen atmosphere. The properties were evaluated through high-temperature tensile tests at 800 °C, oxidation tests, and area-specific resistance (ASR) measurements. Microstructural characterization was conducted using x-ray diffraction (XRD), scanning electron microscope (SEM) with energy-dispersive spectroscope (EDS). The results indicated that with an increase in Cr content, the strength of the powder metallurgy ferritic stainless steel specimens increased, while the elongation decreased at 800°C. Additionally, oxidation mass gain decreased, and ASR decreased. Commercially available ZMG232 ferritic stainless steel was employed for high-temperature mechanical, oxidation, and electrical properties comparison. Compared to ZMG232, the high-temperature yield strength and tensile strength of powder metallurgy ferritic stainless steel specimens were higher with 22 wt.% and 26 wt.% Cr content. And with 17 wt.% Cr content, there was a significant difference in oxidation mass gain and ASR. However, with 22 wt.% and 26 wt.% Cr content, oxidation mass gain and ASR were relatively close, indicated that the high Cr content powder metallurgy ferritic stainless steel in this study can be an alternative to the commercially available ZMG232 ferritic stainless steel.

Comparative study on oxidation behavior and electrical conductivity of Crofer22 and STS444 alloys

Initial stage oxidation corrosion of commercial ferritic stainless steels with different Cr contents at 650 °C for solid oxide fuel cells

Fabricating a MnCo coating to improve oxidation resistance and electrical conductivity of Crofer22H alloy as SOFC interconnect

Influence of Cr Content on the Mechanical, Oxidation, and Electrical Properties of Powder Metallurgy Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Metallic interconnects for solid oxide fuel cell: Performance of reactive element oxide coating during long time exposure

Ferritic Steel Interconnect Used in Solid Oxide Fuel Cell

Metallic Interconnects for Solid Oxide Fuel Cell: Performance of Reactive Element Oxide Coating During 10, 20 and 30 Months Exposure

The effect of surface treatment on the oxidation of ferritic stainless steels used for solid oxide fuel cell interconnects

High Temperature Oxidation Behavior of SUS430 SOFC Interconnects with Mn-Co Spinel Coating in Air

Metallic Interconnect Materials Used in Solid Oxide Fuel Cell

High temperature oxidation and chromium volatilisation of AISI 430 stainless steel coated by Mn-Co and Mn-Co-Cu oxides for SOFC interconnect application

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

Ni–Co/ZrO2 Composite Coatings via Electroless Plating on Crofer 22APU for SOFC Interconnect Applications: Oxidation and Chromium Vaporization Behavior

The suitability performance of Sr2Fe1.5Mo0.5O6-δ-coated SUS430 for SOFC interconnect application

Experimental Investigation of the Initial Stage of the Oxidation Mechanism of Co Coating for Solid Oxide Fuel Cell Interconnects at 650 °C

Research Progresses in the Preparation of Spinel Coatings on the Surface of SOFC Ferrite Stainless Steel Interconnectors

The electrical property of MnCo2O4 and its application for SUS 430 metallic interconnect

Evaluation of Protective La0.67Sr0.33MnO3–δ Coatings on Various Stainless Steels Used for Solid Oxide Fuel Cell Interconnects

Characterization of the conductive protection layers on alloy interconnect for SOFC

Effect of Rare Earths on Electrical Conductivity and Oxidation Resistance of Ferritic Fe-22Cr Alloys

Change in the Microstructure of Ferritic Stainless Steel with Surface Roughness and the Number of Thermal Cycles