Abstract:This study aims to investigate the influence of Cr content on the high-temperature mechanical, oxidation, and electrical properties of powder metallurgy ferritic stainless steel for solid oxide fuel cell (SOFC) interconnect. To achieve this objective, ferritic stainless steel water-atomized powders with different Cr content were first compacted and then sintered at 1380 °C for 2 h under hydrogen atmosphere. The properties were evaluated through high-temperature tensile tests at 800 °C, oxidation tests, and area-specific resistance (ASR) measurements. Microstructural characterization was conducted using x-ray diffraction (XRD), scanning electron microscope (SEM) with energy-dispersive spectroscope (EDS). The results indicated that with an increase in Cr content, the strength of the powder metallurgy ferritic stainless steel specimens increased, while the elongation decreased at 800°C. Additionally, oxidation mass gain decreased, and ASR decreased. Commercially available ZMG232 ferritic stainless steel was employed for high-temperature mechanical, oxidation, and electrical properties comparison. Compared to ZMG232, the high-temperature yield strength and tensile strength of powder metallurgy ferritic stainless steel specimens were higher with 22 wt.% and 26 wt.% Cr content. And with 17 wt.% Cr content, there was a significant difference in oxidation mass gain and ASR. However, with 22 wt.% and 26 wt.% Cr content, oxidation mass gain and ASR were relatively close, indicated that the high Cr content powder metallurgy ferritic stainless steel in this study can be an alternative to the commercially available ZMG232 ferritic stainless steel.

Ferritic Steel Interconnect Used in Solid Oxide Fuel Cell

Metallic Interconnect Materials Used in Solid Oxide Fuel Cell

Progress of Interconnect Materials Used for SOFC

Protective/Conductive Coatings on Ferritic Stainless Steels for Solid Oxide Fuel Cell Interconnect Applications

Influence of Cr Content on the Mechanical, Oxidation, and Electrical Properties of Powder Metallurgy Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Perspectives on the metallic interconnects for solid oxide fuel cells

Research Progresses in the Preparation of Spinel Coatings on the Surface of SOFC Ferrite Stainless Steel Interconnectors

Cr-Based Alloy Used as Interconnect in Solid Oxide Fuel Cells

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

Discussion on some problems about the study of metallic interconnect for SOFC

SOFC ' s Interconnects Materials Development

Properties of Fe–Cr Based Alloys As Interconnects in a Solid Oxide Fuel Cell

CHAPTER 6 Development of SOFC Interconnect Stainless Steels

Mechanical reliability and life prediction of coated metallic interconnects within solid oxide fuel cells

Comparative study on oxidation behavior and electrical conductivity of Crofer22 and STS444 alloys

Characterization of Metallic Interconnects Extracted from Solid Oxide Fuel Cell Stacks Operated up to 20,000 h in Real Life Conditions: The Air Side

Initial stage oxidation corrosion of commercial ferritic stainless steels with different Cr contents at 650 °C for solid oxide fuel cells

The Preparation and Properties of Ti(Nb)-Si-C Coating on the Pre-Oxidized Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

CrxN/Mn1.7Cu1.3 coating on ferritic stainless steel for solid oxide fuel cell interconnects

The effect of surface treatment on the oxidation of ferritic stainless steels used for solid oxide fuel cell interconnects

Cu doped Mn-Co spinel protective coating on ferritic stainless steels for SOFC interconnect applications