Abstract:This study aims to investigate the influence of Cr content on the high-temperature mechanical, oxidation, and electrical properties of powder metallurgy ferritic stainless steel for solid oxide fuel cell (SOFC) interconnect. To achieve this objective, ferritic stainless steel water-atomized powders with different Cr content were first compacted and then sintered at 1380 °C for 2 h under hydrogen atmosphere. The properties were evaluated through high-temperature tensile tests at 800 °C, oxidation tests, and area-specific resistance (ASR) measurements. Microstructural characterization was conducted using x-ray diffraction (XRD), scanning electron microscope (SEM) with energy-dispersive spectroscope (EDS). The results indicated that with an increase in Cr content, the strength of the powder metallurgy ferritic stainless steel specimens increased, while the elongation decreased at 800°C. Additionally, oxidation mass gain decreased, and ASR decreased. Commercially available ZMG232 ferritic stainless steel was employed for high-temperature mechanical, oxidation, and electrical properties comparison. Compared to ZMG232, the high-temperature yield strength and tensile strength of powder metallurgy ferritic stainless steel specimens were higher with 22 wt.% and 26 wt.% Cr content. And with 17 wt.% Cr content, there was a significant difference in oxidation mass gain and ASR. However, with 22 wt.% and 26 wt.% Cr content, oxidation mass gain and ASR were relatively close, indicated that the high Cr content powder metallurgy ferritic stainless steel in this study can be an alternative to the commercially available ZMG232 ferritic stainless steel.

Properties of Fe–Cr Based Alloys As Interconnects in a Solid Oxide Fuel Cell

Cr-Based Alloy Used as Interconnect in Solid Oxide Fuel Cells

Metallic Interconnect Materials Used in Solid Oxide Fuel Cell

Metallic Co with Reactive Element Oxide Composite Coatings for Solid Oxide Fuel Cell Interconnect Applications

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

Development of Coating Materials on Alloy Interconnect in Solid Oxide Fuel Cell

Influence of Cr Content on the Mechanical, Oxidation, and Electrical Properties of Powder Metallurgy Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Protective coatings for Cr2O3-forming interconnects of solid oxide fuel cells

Metallic Interconnects for Solid Oxide Fuel Cell: Performance of Reactive Element Oxide Coating During 10, 20 and 30 Months Exposure

Effects of Mn concentration on durability of Fe-Cr ferritic steels dispersed with La 2 O 3 for solid oxide fuel cell interconnects

Metallic interconnects for solid oxide fuel cell: Performance of reactive element oxide coating during long time exposure

Research of Fe-Cr Alloys Properties at High Temperature

Initial stage oxidation corrosion of commercial ferritic stainless steels with different Cr contents at 650 °C for solid oxide fuel cells

Comparison of iron and copper doped manganese cobalt spinel oxides as protective coatings for solid oxide fuel cell interconnects

Ferritic Steel Interconnect Used in Solid Oxide Fuel Cell

The Preparation and Properties of Ti(Nb)-Si-C Coating on the Pre-Oxidized Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Effect of Temperature and Water Content on the Oxidation Behaviour and Cr Evaporation of High-Cr Alloys for SOFC Cathode Air Preheaters

Efficient FeCoNi/CeO 2 coatings for solid oxide fuel cell steel interconnect applications

Evaluation of Protective La0.67Sr0.33MnO3–δ Coatings on Various Stainless Steels Used for Solid Oxide Fuel Cell Interconnects

Fe doped Ni–Co alloy by electroplating as protective coating for solid oxide fuel cell interconnect application

Mechanical characterization of oxide coating–interconnect interfaces for solid oxide fuel cells