Abstract:The evolution of phase composition and mechanical properties and the formation of oxide layers on Fe40–xNiCoCrAlx (x = 5 and 10 at.%) alloys in long-term oxidation at 900 and 1000°C were studied. In the initial cast state, depending on the aluminum content and valence electron concentration, the alloys contain only an fcc solid solution (VEC = 8 e/a) or a mixture of fcc and bcc phases (VEC = = 7.75 e/a). Thin continuous oxide scales containing Cr2O3 and NiCr2O4 spinel formed on the surface of both alloys oxidized at 900°C for 50 h. A further increase in the annealing time to 100 h leads to the formation of aluminum oxide Al2O3 in the scale on the Fe30Ni25Co15Cr20Al10 alloy, having high protective properties. An increase in the oxidation temperature to 1000°C results in partial failure of the protective layer on the alloy with 10 at.% Al. Long-term holding at 900°C (100 h) + 1000°C (50 h) does not change the phase composition of the Fe35Ni25Co15Cr20Al5 alloy matrix, being indicative of its high thermal stability. In the two-phase Fe30Ni25Co15Cr20Al10 alloy, the quantitative ratio of solid solutions sharply changes: the amount of the bcc phase increases from 4 to 54 wt.% and its B2-type ordering is observed. The mechanical characteristics of the starting alloys and those after long-term high-temperature annealing were determined by automated indentation. The hardness (HIT) and elastic modulus (E) of the cast Fe35Ni25Co15Cr20Al5 alloy are equal to 2 and 147 GPa, respectively, and decrease to 1.8 and 106 GPa after a series of long-term annealing operations. The Fe30Ni25Co15Cr20Al10 alloy shows the opposite dependence: HIT increases from 2.5 in the initial state to 3.1 GPa after annealing and E decreases from 152 to 134 GPa. This indicates that the Fe30Ni25Co15Cr20Al10 alloy is promising as a high-temperature oxidation-resistant and creep-resistant material.

Research of Fe-Cr Alloys Properties at High Temperature

Thermophysical Properties and High Temperature Oxidation Behavior of FeCrNiAl0.5 Multi-Component Alloys

The oxidation resistance behavior of the new type Fe-Cr based superalloys

Exploring the high-temperature steam oxidation behaviors of the lean-Cr (7–10 wt%) FeCrAl alloys

Structural State of High-Entropy Fe40–xNiCoCrAlx Alloys in High-Temperature Oxidation

Thermal Performance Determination of Binary Fe-Al Alloys at Elevated Temperatures

Properties of Fe–Cr Based Alloys As Interconnects in a Solid Oxide Fuel Cell

Thermal stability of microstructures and mechanical properties in a Fe-based Fe-Cr-Mn-Cu-Mo multi-component alloy

High Thermal Stability and Oxidation Behavior of FeCrNiAl-based Medium-Entropy Alloys Prepared by Powder Metallurgy

Studies on As-Cast Microstructure and Oxidation Behavior of the FeCrBAl Alloys at 1073 K

Stability of FeCrNiTiAl high-entropy alloy at high temperature

The Mechanical Properties of Fe-36.5Al and Its Cr or Ti Containing Alloys at Elevated Temperature

Towards Superior High Temperature Properties in Low Density AlCrFeNiTi Compositionally Complex Alloys

Oxidation Behaviors of FeCrNiAl High Entropy Alloy and Its Microstructure Evolution

High-Temperature Mechanical Behavior of Cobalt-Free FeMnCrNi(Al) High-Entropy Alloys

High Temperature Oxidation Behavior of Al0.5CrCoFeNi High Entropy Alloy

Effect of temperature on mechanical properties of Al0.5CoCrCuFeNi wrought alloy

Oxidation behavior and high-temperature tensile properties of Fe-9Cr-(Mo, Mo/Ni) alloys

Effect of TM (tm=fe, Mn, Cr) Alloying on the High Temperature Properties and Strengthening Mechanism of Cf/Al Composites

Effect of aluminium and silicon on high temperature oxidation resistance of Fe-Cr-Ni heat resistant steel

Element diffusion behaviors at high temperature and their effects on microstructure and tribological properties of Cr2O3 films