Abstract:The evolution of phase composition and mechanical properties and the formation of oxide layers on Fe40–xNiCoCrAlx (x = 5 and 10 at.%) alloys in long-term oxidation at 900 and 1000°C were studied. In the initial cast state, depending on the aluminum content and valence electron concentration, the alloys contain only an fcc solid solution (VEC = 8 e/a) or a mixture of fcc and bcc phases (VEC = = 7.75 e/a). Thin continuous oxide scales containing Cr2O3 and NiCr2O4 spinel formed on the surface of both alloys oxidized at 900°C for 50 h. A further increase in the annealing time to 100 h leads to the formation of aluminum oxide Al2O3 in the scale on the Fe30Ni25Co15Cr20Al10 alloy, having high protective properties. An increase in the oxidation temperature to 1000°C results in partial failure of the protective layer on the alloy with 10 at.% Al. Long-term holding at 900°C (100 h) + 1000°C (50 h) does not change the phase composition of the Fe35Ni25Co15Cr20Al5 alloy matrix, being indicative of its high thermal stability. In the two-phase Fe30Ni25Co15Cr20Al10 alloy, the quantitative ratio of solid solutions sharply changes: the amount of the bcc phase increases from 4 to 54 wt.% and its B2-type ordering is observed. The mechanical characteristics of the starting alloys and those after long-term high-temperature annealing were determined by automated indentation. The hardness (HIT) and elastic modulus (E) of the cast Fe35Ni25Co15Cr20Al5 alloy are equal to 2 and 147 GPa, respectively, and decrease to 1.8 and 106 GPa after a series of long-term annealing operations. The Fe30Ni25Co15Cr20Al10 alloy shows the opposite dependence: HIT increases from 2.5 in the initial state to 3.1 GPa after annealing and E decreases from 152 to 134 GPa. This indicates that the Fe30Ni25Co15Cr20Al10 alloy is promising as a high-temperature oxidation-resistant and creep-resistant material.

Effect of Al and Ti on High-Temperature Oxidation Behavior of CoCrFeNi-Based High-Entropy Alloys

Effect of Ti Addition on the Microstructure and High-Temperature Oxidation Property of AlCoCrFeNi High-Entropy Alloy

High Temperature Oxidation Behavior of Al0.5CrCoFeNi High Entropy Alloy

Microstructural Stability and High-Temperature Oxidation Behavior of Al0.25CoCrCuFeNi High Entropy Alloy

Structural State of High-Entropy Fe40–xNiCoCrAlx Alloys in High-Temperature Oxidation

High-temperature oxidation behaviour of low-entropy alloy to medium- and high-entropy alloys

Effect of Cr Content on the High Temperature Oxidation Behavior of FeCoNiMnCrx Porous High-Entropy Alloys

Improving high-temperature oxidation behavior by modifying Al and Co content in Al-Co-Cr-Fe-Ni high-entropy alloy

Wear and oxidation resistances of AlCrFeNiTi-based high entropy alloys

Study on Precipitation in (cocrfemnni)90al6ti4 High Entropy Alloy

Effect of Cr content on the high temperature oxidation behavior of FeCoNiMnCr x porous high-entropy alloys

High-Temperature Oxidation Behavior of Al-Co-Cr-Ni-(Fe or Si) Multicomponent High-Entropy Alloys

Effect of Ti and C addition on oxidation resistance of FeCoCrNiMn high entropy alloys prepared by powder metallurgy

High-Temperature Oxidation and Phase Stability of AlCrCoFeNi High Entropy Alloy: Insights from In Situ HT-XRD and Thermodynamic Calculations

High temperature and short-term oxidation behavior of CoCrCu1.2FeNi high entropy alloy in solid and semi-solid state

High Temperature Oxidation Resistance of NiCoCrAl High Entropy Alloy Coating on the TiAl Alloy

Effect of Ti Content on the Microstructure and Properties of CoCrFeNiMnTix High Entropy Alloy

Effect of Ti on Characterization and Properties of CoCrFeNiTix High Entropy Alloy Prepared Via Electro-Deoxidization of the Metal Oxides and Vacuum Hot Pressing Sintering Process

Clarifying the effects of composition and phase stabilization on the oxidation resistance in AlCoCrFeNiTi series high-entropy alloys at 1100 °C

Effect of Ti content on Magnetic and Electrochemical Corrosion Properties of FeCoCrNi High Entropy Alloys

High-Temperature Oxidation and Microstructural Changes of Al0.75CoCrFeNi High-Entropy Alloy at 900 and 1100 °C