Abstract:This study aims to investigate the influence of Cr content on the high-temperature mechanical, oxidation, and electrical properties of powder metallurgy ferritic stainless steel for solid oxide fuel cell (SOFC) interconnect. To achieve this objective, ferritic stainless steel water-atomized powders with different Cr content were first compacted and then sintered at 1380 °C for 2 h under hydrogen atmosphere. The properties were evaluated through high-temperature tensile tests at 800 °C, oxidation tests, and area-specific resistance (ASR) measurements. Microstructural characterization was conducted using x-ray diffraction (XRD), scanning electron microscope (SEM) with energy-dispersive spectroscope (EDS). The results indicated that with an increase in Cr content, the strength of the powder metallurgy ferritic stainless steel specimens increased, while the elongation decreased at 800°C. Additionally, oxidation mass gain decreased, and ASR decreased. Commercially available ZMG232 ferritic stainless steel was employed for high-temperature mechanical, oxidation, and electrical properties comparison. Compared to ZMG232, the high-temperature yield strength and tensile strength of powder metallurgy ferritic stainless steel specimens were higher with 22 wt.% and 26 wt.% Cr content. And with 17 wt.% Cr content, there was a significant difference in oxidation mass gain and ASR. However, with 22 wt.% and 26 wt.% Cr content, oxidation mass gain and ASR were relatively close, indicated that the high Cr content powder metallurgy ferritic stainless steel in this study can be an alternative to the commercially available ZMG232 ferritic stainless steel.

Metallic Interconnect Materials Used in Solid Oxide Fuel Cell

Ferritic Steel Interconnect Used in Solid Oxide Fuel Cell

Cr-Based Alloy Used as Interconnect in Solid Oxide Fuel Cells

Perspectives on the metallic interconnects for solid oxide fuel cells

Development of Coating Materials on Alloy Interconnect in Solid Oxide Fuel Cell

Progress of Interconnect Materials Used for SOFC

Protective/Conductive Coatings on Ferritic Stainless Steels for Solid Oxide Fuel Cell Interconnect Applications

Discussion on some problems about the study of metallic interconnect for SOFC

Properties of Fe–Cr Based Alloys As Interconnects in a Solid Oxide Fuel Cell

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

Evaluation of Protective La0.67Sr0.33MnO3–δ Coatings on Various Stainless Steels Used for Solid Oxide Fuel Cell Interconnects

Influence of Cr Content on the Mechanical, Oxidation, and Electrical Properties of Powder Metallurgy Ferritic Stainless Steel for Solid Oxide Fuel Cell Interconnect

Effect of Rare Earth Y and Metal X (Co, Mn, Ni, Cu) Elements on Cr Diffusion Behavior of SOFC Metallic Interconnect

Metallic Interconnects for Solid Oxide Fuel Cell: Performance of Reactive Element Oxide Coating During 10, 20 and 30 Months Exposure

Effects of Mn concentration on durability of Fe-Cr ferritic steels dispersed with La 2 O 3 for solid oxide fuel cell interconnects

Metallic interconnects for solid oxide fuel cell: Performance of reactive element oxide coating during long time exposure

Mechanical reliability and life prediction of coated metallic interconnects within solid oxide fuel cells

Progress in SOFC Metallic Interconnect Coating

Metallic Co with Reactive Element Oxide Composite Coatings for Solid Oxide Fuel Cell Interconnect Applications

Research Progresses in the Preparation of Spinel Coatings on the Surface of SOFC Ferrite Stainless Steel Interconnectors

Protective coatings for Cr2O3-forming interconnects of solid oxide fuel cells