Abstract:La0.6Sr0.4CoO3 (LSC) coatings with a thickness of 50-100 µm were deposited on Fe-25Cr ferritic stainless steel (DIN 50049) via screen printing. The required suspension had been prepared using fine LSC powders synthesised using EDTA gel processes. In its bulk form, the LSC consisted entirely of the rhombohedral phase with space group R-3c, and it exhibited high electrical conductivity (~144 S·cm-1). LSC-coated steel was oxidised in air at 1073 K, i.e., under conditions corresponding to SOFC cathode operation, for times of up to 144 h. The in situ electrical resistance of the steel/La0.6Sr0.4CoO3 layered system during oxidation was measured. The products formed on the samples after the oxidation reaction resulting from exposure to the corrosive medium were investigated using XRD, SEM-EDS, and TEM-SAD. The microstructural, nanostructural, phase, and chemical analysis of films was performed with a focus on the film/substrate interface. It was determined that the LSC coating interacts with the oxidised steel in the applied conditions, and a multi-layer interfacial zone is formed. Detailed TEM-SAD observations indicated the formation of a main layer consisting of SrCrO4, which was the reaction product of (La,Sr)CoO3, and the Cr2O3 scale formed on the metal surface. The formation of the SrCrO4 phase resulted in improved electrical conductivity of the investigated metal/ceramics layered composite material, as demonstrated by the low area-specific resistance values of 5 mΩ·cm2, thus making it potentially useful as a SOFC interconnect material operating at the tested temperature. In addition, the evaporation rate of chromium measured for the uncoated steel and the steel/La0.6Sr0.4CoO3 layered system likewise indicates that the coating is capable of acting as an effective barrier against the formation of volatile compounds of chromium.

Characterization of the conductive protection layers on alloy interconnect for SOFC

Low-temperature Solid Oxide Fuel Cells with Novel La0.6Sr0.4Co0.8Cu0.2O3−δ Perovskite Cathode and Functional Graded Anode

Characterization of La0.8Sr0.2Co0.5Mn0.5O3-δ Coating on Alloy Interconnect in SOFC

High Temperature Oxidation Behavior of SUS430 SOFC Interconnects with Mn-Co Spinel Coating in Air

Evaluation of Protective La0.67Sr0.33MnO3–δ Coatings on Various Stainless Steels Used for Solid Oxide Fuel Cell Interconnects

The electrical property of MnCo2O4 and its application for SUS 430 metallic interconnect

Supersonic spray derived Cu–Co oxide coating on SUS441 to protect the metallic interconnect and to increase stability of SOFC cathode

Oxidation and electrical behavior of Ni-Mn3O4-La2O3-coated SOFC interconnect steel

High-entropy FeCoNiMnCu alloy coating on ferritic stainless steel for solid oxide fuel cell interconnects

Stability Study on a Novel Micro Structure Configuration of Cathode Contact Layer for Solid Oxide Fuel Cell Stack

Validation and Electrochemical Characterization of LSCF Cathode Deposition on Metal Supported SOFC

Effect of MnCoNiFeCu Alloy on Oxidation Behavior and Electrical Performance of AISI 441 for SOFC Interconnect Application

The suitability performance of Sr2Fe1.5Mo0.5O6-δ-coated SUS430 for SOFC interconnect application

Conducting Property and Performance Evaluation of LNF As Cathode Current Contact Layer in Solid Oxide Fuel Cell

Preparation, Evaluation, and Application of SUS430/441 Interconnect with Mn-Co Coating in Solid Oxide Fuel Cells

Characterization of the Microstructure and Electrical Conductivity of Plasma-Sprayed La0.5Sr0.5CoO3 Coating

Plasma spray coating on interconnector toward promoted solid oxide fuel cells and solid oxide electrolysis cells

Exploration of Co-Fe Alloy Precipitation and Electrochemical Behavior Hysteresis Using Lanthanum and Cobalt Co-Substituted SrFeO3-δ SOFC Anode

Physicochemical Properties of (La,Sr)CoO3 Thick Films on Fe-25Cr Steel under Exposure to SOFC Cathode Operating Conditions

Study on the Conductivity of La0.4Sr1.6CoNbO6-δ as an Electrode Material for Symmetrical SOFC

Performance and In-Situ Densification of Mn-Co Spinel Coating on SUS430/441 Interconnect by Spraying Method